The study focuses on in vitro tracing of some fundamental changes that emerge in teeth at the initial stage of caries development using multiple approaches. The research was conducted on a mostly sound maxillary molar tooth but with a clearly visible natural proximal white spot lesion (WSL). Values of mineral density, reduced Young’s modulus, indentation hardness and creep as well as the molecular composition and surface microstructure of the WSL and bordering dentine area were studied. The results obtained were compared to those of sound enamel and dentine on the same tooth. A decrease of mechanical properties and mineral density both for the WSL and bordering dentine was detected in comparison to the sound counterparts, as well as increase of creep for the enamel WSL. Differences in molecular composition and surface microstructure (including the indenter impressions) were found and described. WSL induces a serious change in the state of not only the visually affected enamel but also surrounding visually intact enamel and dentine in its vicinity. The results provide the basis for future studies of efficacy of minimal invasive treatments of caries.

The present paper addresses the problem of identification of microstructural, nanomechanical, and tribological properties of thin films of tantalum (Ta) and its compounds deposited on stainless steel substrates by direct current magnetron sputtering. The compositions of the obtained nanostructured films were determined by energy dispersive spectroscopy. Surface morphology was investigated using atomic force microscopy (AFM). The coatings were found to be homogeneous and have low roughness values (<10 nm). The values of microhardness and elastic modulus were obtained by means of nanoindentation. Elastic modulus values for all the coatings remained unchanged with different atomic percentage of tantalum in the films. The values of microhardness of the tantalum films were increased after incorporation of the oxygen and nitrogen atoms into the crystal lattice of the coatings. The coefficient of friction, CoF, was determined by the AFM method in the “sliding” and “plowing” modes. Deposition of the coatings on the substrates led to a decrease of CoF for the coating-substrate system compared to the substrates; thus, the final product utilizing such a coating will presumably have a longer service life. The tantalum nitride films were characterized by the smallest values of CoF and specific volumetric wear.

The transition metal oxynitrides are a coating material with decorative features due to their adjustable color and good mechanical properties. The purpose of the research was to study the effect of the relative oxygen concentration O_2(x) = O₂/(N₂ + O₂) in particular on adhesion, but also on the color, structural and mechanical properties of ZrON coatings synthesized by cathodic arc evaporation on HS6-5-2 steel substrates. The surface morphology, phase and chemical composition and mechanical properties were determined using scanning electron microscopy, X-ray diffraction, wavelength dispersive X-ray spectroscopy, nanoindentation and scratch test. It was found that color of the coatings changed from light yellow for ZrN first to gold and then to graphite for Zr-O phase with increase of oxygen concentration. X-ray diffraction patterns showed that the phase separation of ZrN and ZrO₂ occurred for about 35 at.% of oxygen in the coating. Increase in oxygen concentration in the coatings led to decrease in crystallite size from about 20 nm for ZrN to about 5 nm for coatings with about 35 at.% of oxygen and about 25 at.% of nitrogen. An increase in hardness from about 26 GPa for ZrN to about 30 GPa for coating with small concentration of oxygen (about 9 at.%) and then decrease to about 15 GPa was observed. Adhesion of Zr-O-N coatings demonstrated strong dependence on oxygen concentration. Critical load for ZrN is about 80 N and decreases with oxygen concentration increase to about 30 N for ZrO₂.

An effective mathematical model is proposed to describe experiments on the indentation of samples with layered or functionally graded coatings. The model is based on the elastic contact problem...

In our research, we have focused on the estimation of tribological and mechanical characteristics of self-organized copper film, formed through a friction of brass-steel pair in aqueous solutions of carbolic acid. We have found out that self-organized copper film formed through a friction interaction of pair brass-steel is nanostructural. The data obtained through the indentation of self-organized copper films indicated size effect. With an increasing load and contact area of interacting bodies, the coefficient of friction first drops sharply with an increasing normal load and then begins to grow. We have found out that the adhesion component of friction contributes to the friction coefficient at small loads. We have shown that the hardness of self-organized copper films formed at friction in aqueous solutions of acids increases upon shifting from acetic to caproic acid.