Silane coupling agents (SCAs) with different organofunctional groups were coated on the surfaces of Al₂O₃ ceramic particles through hydrolysis and condensation reactions, and the SCA-coated Al₂O₃ ceramic particles were dispersed in a commercial photopolymer based on interpenetrating networks (IPNs). The organofunctional groups that have high radical reactivity and are more effective in UV curing systems are usually functional groups based on acryl, such as acryloxy groups, methacrloxy groups, and acrylamide groups, and these silane coupling agents seem to improve interfacial adhesion and dispersion stability. The coating morphology and the coating thickness distribution of SCA-coated Al₂O₃ ceramic particles according to the different organofunctional groups were observed by FE-TEM. The initial dispersibility and dispersion stability of the SCA-coated Al₂O₃/High-temp composite solutions were investigated by relaxation NMR and Turbiscan. The rheological properties of the composite solutions were investigated by viscoelastic analysis and the mechanical properties of 3D-printed objects were observed with a nanoindenter.

A 3YSZ (3 mol% yttria-stabilized zirconia) ceramic green body with 50 vol% of ceramic content was 3D-printed by supportless stereolithography under optimal drying, debinding, and sintering conditions in order to achieve high strength and density. The viscosity and flowability of the ceramic nanocomposite resins were optimized by adjusting the amounts of non-reactive diluents. The ceramic 3D-printed objects have a high polymer content compared to ceramics samples manufactured by conventional manufacturing processes, and the attraction between layers is weak because of the layer-by-layer additive method. This causes problems such as layer separation and cracking due to internal stress generated when materials such as solvents and polymers are separated from the objects during the drying and debinding processes; therefore, the drying and debinding conditions of 3YSZ ceramic 3D-printed objects were optimized based on thermogravimetry–differential thermal analysis. The sintering conditions at various temperatures and times were analyzed using X-ray diffraction, SEM, and flexural strength analysis, and the body of the 3YSZ ceramic 3D-printed object that sintered at 1450 °C for 150 min had a relative density of 99.95% and flexural strength of 1008.5 MPa. This study widens the possibility of manufacturing ceramic 3D-printed objects with complex shapes, remarkable strength, and unique functionality, enabling their application in various industrial fields.

Ceramics are high-strength and high-temperature resistant materials that are used in various functional parts. However, due to the high strength and brittleness properties, there are many difficulties in the fabrication of complex shapes. Therefore, there are many studies related to the fabrication of ceramic parts using 3D printing technology optimized for complex shapes. Among them, studies using photo-polymerization (PP) 3D printing technology with excellent dimensional accuracy and surface quality have received the most widespread attention. To secure the physical properties of sintered ceramic, the content and distribution of materials are important. This study suggests a novel 3D printing process based on a high-viscosity composite resin that maximizes the content of zirconia ceramics. For reliable printing, the developed 3D printers that can adjust the process environment were used. To minimize warpage and delamination, the divided micro square pattern images were irradiated in two separate intervals of 1.6 s each while maintaining the internal chamber temperature at 40 °C. This contributed to improved stability and density of the sintered structures. Ultimately, the ceramic parts with a Vickers hardness of 12.2 GPa and a relative density of over 95% were able to be fabricated based on a high-viscosity resin with 25,000 cps.