Natural cellulose, a sustainable bioresource, is highly abundant in nature. Cellulosic materials, particularly those that explore and employ such materials for industrial use, have recently attracted significant global attention in the field of material science because of the unique properties of cellulose. The hydroxyl groups enable the formation of intra- and inter-molecular hydrogen bonding and the arrangement of cellulose chains in a highly ordered crystalline zone, with the remaining disordered structure referred to as an amorphous region. The crystalline areas of cellulose are well-known as cellulose nanocrystals (CNCs). In the present study, we extracted CNCs from pure cellulose isolated from waste jute fibers by sulfuric acid hydrolysis, followed by characterization. Pure cellulose was isolated from jute fibers by treating with sodium hydroxide (20% w/w) and anthraquinone (0.5%) solution at 170 °C for 2 h, followed by bleaching with chlorine dioxide and hydrogen peroxide solution. CNCs were isolated from pure cellulose by treating with different concentrations (58% to 62%) of sulfuric acid at different time intervals (20 min to 45 min). The FTIR study of the CNCs reveals no peak at 1738 cm⁻¹, which confirms the absence of hemicellulose in the samples. The CNCs obtained after 45 min of acid hydrolysis are rod-shaped, having an average length of 800 ± 100 nm and width of 55 ± 10 nm, with a high crystallinity index (90%). Zeta potential significantly increased due to the attachment of SO₄²⁻ ions on the surface of CNC from −1.0 mV to about −30 mV, with the increment of the reaction time from 20 min to 45 min, which proved the higher stability of CNC suspension. Crystallinity increased from 80% to 90% when the reaction time was increased from 20 to 45 min, respectively, while a crystallite size from 2.705 to 4.56 nm was obtained with an increment of the acid concentration. Acid hydrolysis enhanced crystallinity but attenuated the temperature corresponding to major decomposition (Tmax) at 260 °C and the beginning of degradation (Ti) at 200 °C due to the attachment of SO₄²⁻ ions on the surface, which decreased the thermal stability of CNC. The second degradation at 360 °C indicated the stable crystal structure of CNC. The endothermic peak at 255 °C in the DTA study provided evidence of sulfated nanocrystal decomposition and the recrystallization of cellulose I to cellulose II, the most stable structure among the other four celluloses. The proposed easy-to-reproduce method can successfully and efficiently produce CNCs from waste jute fibers in a straightforward way.

Millettia peguensis, popular for its ethnopharmacological uses, was employed to evaluate its different pharmacological properties in this study. The analgesic studies of the plant have been performed by acetic acid-induced writhing and formalin-induced licking tests respectively, whereas the antidiarrheal experiment was done by castor oil-induced diarrheal test. Besides, antioxidant, cytotoxic, antimicrobial, thrombolytic evaluations were performed by DPPH scavenging with phenol content determination, brine shrimp lethality, disc diffusion and clot lysis methods respectively. Moreover, in silico study of the phytoconstituents was carried out by molecular docking and ADME/T analysis.

Background: Colocasia gigantea, locally named as kochu is well-known due to its various healing power. This research is to investigate the antidiarrheal, antimicrobial and antioxidant possibilities of the methanol soluble extract of Colocasia gigantea. Methods: The antidiarrheal investigation was performed by using in vivo castor oil-induced diarrheal method whereas in vitro antimicrobial and antioxidant investigation have been implemented by disc diffusion and DPPH scavenging method respectively. Moreover, in silico studies were followed by molecular docking analysis of several secondary metabolites that were appraised with Schrödinger-Maestro v11.1 and Biovia Discovery Studio. Results: The induction of plant extract (200 and 400 mg/kg, b.w, p.o) has minimized the castor oil mediated diarrhea by 16.96% (p < 0.01) and 38.89% (p < 0.001) respectively compared to control group. The methanol extract of C. gigantea showed mild sensitivity against almost all the tested strains but it shows high consistency of phenolic content and yielded 67.68 μg/mL of IC₅₀ value in the DPPH test. In the PASS prediction, selected isolated compounds have demonstrated significant antidiarrheal and antimicrobial activity following the Lipinski drug rules which have ascertained efficacy with the compounds in molecular docking study. Conclusion: The results of this scientific research reflects that the methanol soluble extract of C. gigantea is safe and may provide possibilities of alleviation of diarrhea along with being a potential wellspring of antioxidant and antimicrobial agents which can be considered as an alternate source for exploration of new medicinal products in near future.

Three cardenolide glycosides, calotropin (1), frugoside (2), and 4'-O-beta-D-glucopyranosylfrugoside (3), were obtained as the cytotoxic principles of "akond mul" (roots of Calotropis gigantea L.). The cytotoxicity of these compounds against various cell lines of human and mouse origin was tested. They showed similar cell line selectivity to those of cardiac glycosides such as digoxin and ouabain: they are toxic to cell lines of human origin, but not to those from mouse at 2 micrograms/ml.