The verification of the blasting parameters of Ammonium Nitrate Fuel Oil (ANFO) with the addition of microstructured charcoal (MC) produced by destructive wood distillation was performed. Additional investigation of specific surface and pore distribution by the nitrogen adsorption of the two granulations of MC was also carried out. High-resolution scanning electron microscopy was used for morphology evaluation and revealed smoothening of the initially developed external surface of carbon with intensive milling. In addition, the analysis of the thermal properties of the studied samples (TG/DSC) indicated that the size of the microstructured charcoal additives influenced the decomposition temperature of the prepared materials. The explosives containing microstructured charcoal grains of −90 μm underwent decomposition at lower temperatures in comparison with those containing higher sizes of microstructure charcoal grains (−1.18 mm), for which the decomposition temperature reached 292 °C. The obtained results of blasting parameters compared to the results derived from thermodynamic simulation showed the non-ideal character of the explosives (much lower values of blasting parameters than in established thermodynamic models). It was indicated that higher velocities of detonations (VOD) were obtained for non-ideal explosives where finer MC grains were added. Blasting tests confirmed that the studied type of MC can be applied as an additive to the ANFO.

In this study, we examined the influence of microstructured charcoal (MC) when added to ammonium nitrate fuel oil (ANFO) samples. We performed a study that investigated ANFOs structure, crystallinity, and morphology by utilizing infrared spectroscopy (IR), X-ray diffraction (XRD), and scanning electron microscopy (SEM), respectively. MC characteristics were probed by Raman spectroscopy and SEM analysis. SEM analysis indicated how fuel oil (FO) covered ammonium nitrate prill. Moreover, the surface of the MC was covered by specific microfibers and microtubes. The disordered graphitic structure of the MC was also confirmed by Raman spectroscopy. Simulation of blasting properties revealed that the addition of MC should decrease blasting parameters like heat explosion, detonation pressure, and detonation temperature. However, the obtained differences are negligible in comparison with the regular ANFO. All analyses indicated that MC was a good candidate as an additive to ANFO.