Rust Resistance: The rusting of iron and steel can be prevented through the addition of 11% or more chromium. The addition of molybdenum can enhance the corrosion resistance, with a complex interplay between the Cr and Mo atoms. However, if chemical variations exist, corrosion can still occur in localized regions or if the surface layer is mechanically abraded. Duarte et al. (p. 372 ) studied the corrosive failure of an iron-based glassy alloy. A combination of atom probe tomography, electron microscopy, and x-ray diffraction was used to build up a near atomistic picture of local variations in the metal as it was heated and allowed to crystallize, and the impact these processes have on the corrosion resistance.

Graphene, the newest member of the carbon’s family, has proven its efficiency in improving polymers’ resistance against photodegradation, even at low loadings equal to 1 wt% or lower. This protective role involves a multitude of complementary mechanisms associated with graphene’s unique geometry and chemistry. In this review, these mechanisms, taking place during both the initiation and propagation steps of photodegradation, are discussed concerning graphene and graphene derivatives, i.e., graphene oxide (GO) and reduced graphene oxide (rGO). In particular, graphene displays important UV absorption, free radical scavenging, and quenching capabilities thanks to the abundant π-bonds and sp² carbon sites in its hexagonal lattice structure. The free radical scavenging effect is also partially linked with functional hydroxyl groups on the surface. However, the sp² sites remain the predominant player, which makes graphene’s antioxidant effect potentially stronger than rGO and GO. Besides, UV screening and oxygen barriers are active protective mechanisms attributed to graphene’s high surface area and 2D geometry. Moreover, the way that graphene, as a nucleating agent, can improve the photostability of polymers, have been explored as well. These include the potential effect of graphene on increasing polymer’s glass transition temperature and crystallinity.

The effect of low amounts of Cr on glass forming ability and corrosion behavior of Fe(65-x)CrxMo14C15B6 (x = 0, 2, 4, 6, 8,10 at.%) ribbons have been studied. It was found that the reduced glass transition temperature (T-rg) do not change significantly with Cr content. The glass forming ability (GFA) of this system is evaluated by the gamma(m), delta and omega parameters and the alloys containing 4 and 6 at.% were found to be the best glass formers in this system. The temperature interval of the supercooled liquid region (Delta T-x) changed with Cr and was enlarged from 35 K at x = 0 to 50 K at x = 4. Corrosion rates measured by immersion tests in H2SO4 decreased with an increase of chromium content in the alloys. The electrochemical measurements indicate that the alloys containing more than 4 at.% of Cr are spontaneously passivated with low current densities in 0.1 N H2SO4 whereas the alloys with Cr content <4 at.% showed transpassive Mo dissolution. In view of these results, the optimal amount of Cr addition in Fe-Mo-C-B amorphous steels is discussed. (C) 2014 Elsevier B.V. All rights reserved.Peer ReviewedPostprint (published version

Polyester nanocomposites reinforced with graphene nanoplatelets (GnPs) with two different lateral sizes are prepared by high shear mixing, followed by compression molding. The effects of the size and concentration of GnP, as well as of the processing method, on the electrical conductivity and electromagnetic interference (EMI) shielding behavior of these nanocomposites are experimentally investigated. The in-plane electrical conductivity of the nanocomposites with larger-size GnPs is approximately one order of magnitude higher than the cross-plane volume conductivity. According to the SEM images, the compression-induced alignments of GnPs is found to be responsible for this anisotropic behavior. The orientation of the small size GnPs in the composite is not influenced by the compression process as strongly, and consequently, the electrical conductivity of these nanocomposites exhibits only a slight anisotropy. The maximum EMI shielding effectiveness (SE) of 27 dB (reduction of 99.8% of the incident radiation) is achieved at 25 wt.% of the smaller-size GnP loading. Experimental results show that the EMI shielding mechanism of these composites has a strong dependency on the lateral dimension of GnPs. The non-aligned smaller-size GnPs are leveraged to obtain a relatively high absorption coefficient (≈40%). This absorption coefficient is superior to the existing single-filler bulk polymer composite with a similar thickness.

Solid-state batteries (SSBs) have emerged as a potential alternative to conventional Li-ion batteries (LIBs) since they are safer and offer higher energy density. Despite the hype, SSBs are yet to surpass their liquid counterparts in terms of electrochemical performance. This is mainly due to challenges at both the materials and cell integration levels. Various strategies have been devised to address the issue of SSBs. In this review, we have explored the role of graphene-based materials (GBM) in enhancing the electrochemical performance of SSBs. We have covered each individual component of an SSB (electrolyte, cathode, anode, and interface) and highlighted the approaches using GBMs to achieve stable and better performance. The recent literature shows that GBMs impart stability to SSBs by improving Li⁺ ion kinetics in the electrodes, electrolyte and at the interfaces. Furthermore, they improve the mechanical and thermal properties of the polymer and ceramic solid-state electrolytes (SSEs). Overall, the enhancements endowed by GBMs will address the challenges that are stunting the proliferation of SSBs.

Production process was chosen in order to be readily scalable at the industrial level. The resin/graphene mixture was prepared through high shear mixing at six different weight concentrations between 0% and 10%. Samples were subsequently produced by compression molding. The electrical properties were measured both in-the-plane and across-the-plane using, respectively, a four-point probe and a two-electrode system. The two-electrode system was a dielectric spectrometer, and accordingly, the across-the-plane measurements were conducted in the frequency-domain. Mechanical measurements were conducted using conventional three-point bending and impact setups. The percolation threshold was found to be in the range of 3–5 wt.% concentration, for which the conductivity showed a 7 orders of magnitude increase. These results were quite similar to the samples containing around 50 wt.% of glass fibers. Surprisingly, the in-the-plane conductivity was found to be lower than the bulk conductivity, contrary to what was found with the same filler for thermoplastic composites prepared by melt compounding. No significant increase in mechanical properties as a function of filler loading was observed, except maybe a slight increase in the material toughness.