An antibacterial and anti-oxidation composite film was prepared by a casting method using sodium alginate (SA) and apple polyphenols (APPs) as the base material and glycerol as the plasticizer. Silver nanoparticles (AgNPs) were deposited by ultrasonic-assisted electrospray method. The degree of influence of the addition ratio of SA and AgNPs and different ultrasonic time on the mechanical properties, barrier properties, optical properties, and hydrophilicity of the composite film was explored. The composite films were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that the SA: AgNPs ratio of 7:3 and the ultrasonic time for 30 min have the best comprehensive performance, and SA/AgNPs/APP films showed the lowest water vapor permeability value of 0.75 × 10⁻¹¹ g/m·s·Pa. The composite film has good strength and softness, with tensile strength (TS) and elongation at break (E) at 23.94 MPa and 29.18%, respectively. SEM images showed that the surface of the composite film was smooth and the AgNPs’ distribution was uniform. The composite film showed broad antibacterial activity, and the antibacterial activity of Escherichia coli (92.01%) was higher than that of Staphylococcus aureus (91.26%). However, due to the addition of APP, its antioxidant activity can reach 98.39%, which has a synergistic effect on antibacterial activity. For strawberry as a model, the results showed that this composite film can prolong the shelf life of strawberries for about 8 days at 4 °C, effectively maintaining their storage quality. Compared with the commonly used PE(Polyethylene film) film on the market, it has a greater fresh-keeping effect and can be used as an active food packaging material.

Novel fibers containing different ratios of PVA and d-limonene were fabricated using electrospinning for antibacterial active packaging applications. The PVA/d-limonene fibers were thoroughly characterized using a scanning electron microscope, fourier-transform infrared spectrometry, thermal gravimetry, differential scanning calorimetry, tensile tests, and oxygen permeability tests. The results of these analyses showed that the highest tensile strength and elongation at break values of 3.87 ± 0.25 MPa and 55.62 ± 2.93%, respectively, were achieved for a PVA/d-limonene ratio of 7:3 (v/v) and an ultrasonication time of 15 min during processing. This material also showed the lowest oxygen permeation and the best degradability and bacteriostatic properties of all samples.

Collagens were extracted from grass carp skin (GCC), grass carp scales (GSC), and crucian carp skin (CCC) using an acid-enzyme combination method, and their characteristics and self-assembly properties were analyzed. Electrophoretic patterns characterized all three as type I collagens. An ultraviolet analysis identified the optimal wavelengths for collagen detection, while a Fourier transform infrared spectroscopy analysis confirmed the triple-helical structure of the collagens. The GCC, GSC, and CCC had denaturation temperatures of 39.75, 34.49, and 39.05 °C, respectively. All three were shown to self-assemble into fibrils at 30 °C in the presence of NaCl, but the fibril formation rate of CCC (40%) was slightly higher than those of GCC (28%) and GSC (27%). The GSC were shown to form a more strongly intertwined fibril network with a characteristic D-periodicity. The fish collagens extracted in this study have potential applications in the development of functionalized materials.