Mesoporous heterojunction MOF-derived α-Fe₂O₃/ZnO composites were prepared by a simple calcination of α-Fe₂O₃/ZIF-8 as a sacrificial template.

A composite membrane was fabricated from biopolymer chitosan and montmorillonite (MMT) filler as an alternative membrane electrolyte for direct methanol fuel cell (DMFC) application. To first improve the organic–inorganic interfacial morphology, the pristine MMT was pre-treated using 3-glicidoxy propyltrimethoxysilane (GPTMS) surface modifier to produce organophilic MMT (O-MMT). The GPTMS modified MMT was mixed with chitosan in acetic acid solution and cast into membranes. SEM images and FTIR analysis showed that the O-MMT was successfully incorporated into the chitosan polymer matrix. Water and methanol uptake of the Ch/O-MMT composite membranes decreased with increasing O-MMT loadings, but the ion exchange capacity (IEC) value increased. The Ch/O-MMT with 5 wt% O-MMT loading exhibited the best methanol permeability and proton conductivity characteristics among the other Ch/O-MMT membranes, which were 3.03 × 10⁻⁷ cm² s⁻¹ and 4.66 mS cm⁻¹, respectively. All the results obtained from this study can be used to conclude that the chitosan membrane with O-MMT filler is a promising high performance PEM candidate for DMFC application.

The synthesized 3,3-di(indolyl)indolin-2-ones 1a-p showed desired higher α-glucosidase inhibitory activities and lower α-amylase inhibitory activities than standard drug acarbose. Particularly, compound 1i showed favorable higher α-glucosidase % inhibition of 67 ± 13 and lower α-amylase % inhibition of 51 ± 4 in comparison to acarbose with % inhibition activities of 19 ± 5 and 90 ± 2, respectively. Docking studies of selected 3,3-di(indolyl)indolin-2-ones revealed key interactions with the active sites of both α-glucosidase and α-amylase, further supporting the observed % inhibitory activities. Furthermore, the binding energies are consistent with the % inhibition values. The results suggest that 3,3-di(indolyl)indolin-2-ones may be developed as suitable Alpha Glucosidase Inhibitors (AGIs) and the lower α-amylase activities should be advantageous to reduce the side effects exhibited by commercial AGIs.

In this study, chitosan (CS) doped sulphosuccinic acid (SSA)–glycerol (Gly) and modified montmorillonite clay (MMT) were successfully fabricated. The membranes were prepared using the solution casting method. Analysis of morphology and topography using scanning electron microscopy (SEM) and atomic force microscopy (AFM) revealed that the composite membrane with 3 wt% MMT filler, namely CS/MMT-1, possessed the most adequate surface roughness compared to the other fabricated membranes. Furthermore, mechanical characterization of the CS/MMT-1 composite membrane showed that the membrane achieved satisfactory mechanical strength with a value of 39.23 MPa. Proton conductivity of the composite membranes increased as the temperature was increased. The proton conductivity of the CS/MMT-1 composite membrane increased from 1.75 × 10⁻² S cm⁻¹ at 25 °C up to 3.57 × 10⁻² S cm⁻¹ at 80 °C. The CS/MMT-1 composite membrane also exhibited a methanol permeability value that was significantly lower than that of pristine CS, namely 1.22 × 10⁻⁷ cm² s⁻¹ and 12.49 × 10⁻⁷ cm² s⁻¹, respectively. The results of this study show that the fabricated composite membrane can be used as an alternative polymer electrolyte membrane (PEM) for DMFC applications.

This in-depth review of trisindolines covers their natural occurrence in addition to several routes of synthesis and catalysts used. The biological activities of trisindolines have been discussed with a special emphasis on the structure–activity relationship.