This work presents fabricated silica microstructured optical fiber with special equiangular spiral six-ray geometry, an outer diameter of 125 µm (that corresponds to conventional commercially available telecommunication optical fibers of ratified ITU-T recommendations), and induced chirality with twisting of 200 revolutions per minute (or e.g., under a drawing speed of 3 m per minute, 66 revolutions per 1 m). We discuss the fabrication of twisted microstructured optical fibers. Some results of tests, performed with pilot samples of designed and manufactured stellar chiral silica microstructured optical fiber, including basic transmission parameters, as well as measurements of near-field laser beam profile and spectral and pulse responses, are represented.

We present new type of silica graded index laser-optimized multimode optical fibers (LOMF) with extremely enlarged core diameter up to 100 μm and “typical” “telecommunication” cladding diameter 125 μm. This optical fiber was designed for harsh environment Gigabit onboard cable systems and industrial networks. It differs by special optimized graded refractive index profile, providing low differential mode delay (DMD) for selected guided modes. We present some results of tests, performed for manufactured pilot 520 m length of described LOMF 100/125, concerned with its geometry properties as well as key transmission parameters—attenuation and DMD map.

This work presents designed and fabricated silica few-mode optical fiber (FMF) with induced twisting 10 and 66 revolutions per meter, core diameter 11 µm, typical “telecommunication” cladding diameter 125 µm, improved height of quasi-step refractive index profile and numerical aperture 0.22. Proposed FMF supports 4 guided modes over “C”-band. We discussed selection of specified optical fiber parameters to provide desired limited mode number over mentioned wavelength range. Some results of tests, performed with pilot samples of manufactured FMF, are represented, including experimentally measured spectral responses of laser-excited optical signals, that comprise researches and analysis of few-mode effects, occurring after fiber Bragg grating writing.

This work presents a fabricated silica few-mode microstructured optical fiber (MOF) with a special six GeO₂-doped core geometry, an outer diameter of 125 µm (that corresponds to conventional commercially available telecommunication optical fibers), and improved induced twisting up to 500 revolutions per 1 m (under a rotation speed of 1000 revolutions per meter with a drawing speed of ~2 m per minute). The article discusses some technological aspects and issues of manufacturing the above-described twisted MOFs with complicated structures and geometry as GeO₂-doped silica supporting elements for them. We present results of some measurements performed for fabricated samples of chiral silica six-GeO₂-doped-core few-mode MOFs with various orders of twisting and both step and graded refractive indexes of “cores”. These tests contain research on MOF geometrical parameters, attenuation, and measurements of the far-field laser beam profile.

This work presents results of property researches of fabricated samples of silica few-mode optical fiber (FMF) with induced chirality under twisting 10 and 66 revolutions per meter, core diameter 11 µm, typical “telecommunication” cladding diameter 125 µm and improved height of quasi-step refractive index profile. Proposed FMF supports 4 guided modes over “C”-band. We represent results of computed characteristics, as well as experimentally measured spectral responses of laser-excited optical signals, including researches and analysis of few-mode effects, occurring after fiber Bragg grating writing.