As a natural macromolecule-based biomaterial, fish gelatin is used in medical materials for its low pathogen infection risk. However, because of poor mechanical properties, its application has been limited. In this study, microcrystalline cellulose-reinforced fish gelatin (FG/MCC) composite films were prepared with a biological cross-linking agent (genipin) under ultrasonic treatment. SEM micrographs showed that the smooth microstructure of FG film became increasingly disordered with the addition of MCC. The infrared spectrum analysis (FTIR) demonstrated the existence of hydrogen bond interaction between MCC and FG. Compared with the pure FG film, the tensile strength (TS) and modulus of elasticity (MOE) of composite films with MCC were improved, and the elongation at break (EAB) and swelling ratios (SR) were decreased. Ultrasonic treatment could further improve TS, MOE, and SR. When the composite film was prepared with 15% MCC and treated with ultrasound, the TS and MOE increased by 115% and 227%, respectively, while the EAB decreased by 35% and the SR decreased by 4% in comparison with pure FG films. Thermo-gravimetric analysis (TGA) showed that the FG/MCC composite films were stable below 100 °C. The above results indicate that the FG/MCC films have optimistic application prospects in the biomedical field.

Open source 3D printers (OS3DPs) have become increasingly more widespread in recent years because of their ease of use and budget friendliness, with the majority being fused deposition modeling (FDM) printers. However, due to natural deficiencies of the FDM printing methodology, different printing parameters can cause various properties of printed parts. To obtain printed polylactic acid (PLA) parts with improved tensile properties, a tension model of the part and an orthogonal experiment scheme were constructed in this paper. The effects of three printing parameters (layer height, orientation angle (OA) of the part, and print speed) on tensile properties (elastic modulus, tensile strength, and elongation at break) were investigated. The results demonstrated that the printing parameters affected the tensile properties of PLA parts. Larger layer height and lower print speed contributed to the improvement of tensile strength. The OA of the part had the greatest effect on the parts’ elastic modulus and elongation at break among the three parameters. Both layer height and OA of the part affected part tensile strength significantly. In this research, layer height of 0.2 mm and print speed of 20 ~ 30 mm/s are found to be the optimal printing parameters. Adjusting the OA of the part can provide targeted tensile properties, and the parts with the OA of 45° resulted in the lowest tensile strength because the tensile force is only held by fibers parallel to the force orientation instead of all fibers.

Non-powered adaptive systems are attractive in the construction of environment actuators, meteorosensitive architectures, biomedical devices, and soft robotics. Combining hydrophilic materials and anisotropic structures to mimic self-morphing plant structures has been demonstrated as an effective approach to creating artificial hygromorphs. The convenience of 3D printing technologies in shaping programmable complex structures facilitates the imitation of complex anisotropic plant structures. In this research, we constructed a bio-hygromorph using fish swim bladder hydrogel as the hydrophilic material and wood flour-filled polylactic acid (WPLA) scaffold, which was printed with fused deposition modeling (FDM) 3D printing technology (3DP). The environmental benign bio-hygromorph displayed morphing abilities triggered by moisture content changes, as the fish swim bladder hydrogel swelled and shrunk during absorption and desorption cycles. The strain disproportion of the two-layered composite structure in the bio-hygromorph drove the bending deformation. Stress analyses performed with finite element analysis (FEA) also revealed the mechanism behind the moisture content driven morphing of the bio-hygromorph. Notably, the bio-hygromorph exhibited faster response times to moisture absorption than desorption, which may donate actuators’ different attributes in distinct moisture conditions.

Zero liquid discharge (ZLD) is a technique for treating high-salinity brine to obtain freshwater and/or salt using a solar interface evaporator. However, salt accumulation on the surface of the evaporator is a big challenge to maintaining stable water evaporation. In this study, a simple and easy-to-manufacture evaporator, also called a crystallizer, was designed and fabricated by 3D printing. The photothermal layer printed with polylactic acid/carbon composites had acceptable light absorption (93%) within the wavelength zone of 250 nm–2500 nm. The micron-sized voids formed during 3D printing provided abundant water transportation channels inside the crystallizer. After surface hydrophilic modification, the crystallizer had an ultra-hydrophilic channel structure and gravity-assisted salt recovery function. The results revealed that the angles between the photothermal layers affected the efficacy of solar evaporation and the yield of solid salt. The crystallizer with the angle of 90° between two photothermal layers could collect more solid salt than the three other designs with angles of 30°, 60°, and 120°, respectively. The crystallizer has high evaporation and salt crystallization efficiency in a high-salinity brine environment, which is expected to have application potentials in the zero liquid discharge of wastewater and valuable salt recovery.

Antimicrobial Agent Effectiveness in Fish Glue Prepared by Heat Treatment and Enzymatic Hydrolysis of Swim Bladders