Chemical modification of gelatin using epigallocatechin gallate (EGCG) promotes bone formation in vivo. However, further improvements are required to increase the mechanical strength and bone-forming ability of fabricated EGCG-modified gelatin sponges (EGCG-GS) for practical applications in regenerative therapy. In the present study, we investigated whether vacuum heating-induced dehydrothermal cross-linking of EGCG-GS enhances bone formation in critical-sized rat calvarial defects. The bone-forming ability of vacuum-heated EGCG-GS (vhEGCG-GS) and other sponges was evaluated by micro-computed tomography and histological staining. The degradation of sponges was assessed using protein assays, and cell morphology and proliferation were verified by scanning electron microscopy and immunostaining using osteoblastic UMR106 cells in vitro. Four weeks after the implantation of sponges, greater bone formation was detected for vhEGCG-GS than for EGCG-GS or vacuum-heated gelatin sponges (dehydrothermal cross-linked sponges without EGCG). In vitro experiments revealed that the relatively low degradability of vhEGCG-GS supports cell attachment, proliferation, and cell–cell communication on the matrix. These findings suggest that vacuum heating enhanced the bone forming ability of EGCG-GS, possibly via the dehydrothermal cross-linking of EGCG-GS, which provides a scaffold for cells, and by maintaining the pharmacological effect of EGCG.

Especially in pediatric dentistry, prevention by the control of initial lesions prior to cavitation is very important, and application of a pit and fissure sealant is essential to achieve this. Numerous reports have suggested that resin-based sealants are inferior to sealants based on glass-ionomer cement (GIC), because of GIC’s many advantages, such as fluoride ion release properties and its good adhesion to tooth structures. However, the use of GIC is impeded due to its low flexural strength and fracture toughness. In this paper, we developed and characterized an apatite-ionomer cement (AIC) that incorporates hydroxyapatite (HAp) into the GIC; this development was aimed at not only reinforcing the flexural and compressive strength but also improving some functional properties for the creation of the material suitable for sealant. We examined the influence of differences in the compounding conditions of GIC powder, liquid, and HAp on flexural and compressive strengths, fracture toughness, fluoride ion release property, shear bond strength to bovine enamel, surface pH of setting cements, and acid buffer capability. These methods were aimed at elucidating the reaction mechanism of porous spherical-shaped HAp (HApS) in AIC. The following observations were deduced. (1) HAp can improve the mechanical strengths of AIC by strengthening the cement matrix. (2) The functional properties of AIC, such as acid buffer capability, improved by increasing the releasing amounts of various ions including fluoride ions. The novel AIC developed in this study is a clinically effective dental material for prevention and remineralization of tooth and initial carious lesion.

In this study, we aimed to evaluate the effect of the addition of powdery cellulose nanofibers (CNFs) on the mechanical properties of glass ionomer cement (GIC) without negatively affecting its chemical properties. Commercial GIC was reinforced with powdery CNFs (2–8 wt.%) and characterized in terms of flexural strength, compressive strength, diametral tensile strength, and fluoride-ion release properties. Powdery CNFs and samples subjected to flexural strength testing were observed via scanning electron microscopy. CNF incorporation was found to significantly improve the flexural, compressive, and diametral tensile strengths of GIC, and the corresponding composite was shown to contain fibrillar aggregates of nanofibers interspersed in the GIC matrix. No significant differences in fluoride-ion release properties were observed between the control GIC and the CNF-GIC composite. Thus, powdery CNFs were concluded to be a promising GIC reinforcement agent.

Glass-ionomer-cement (GIC) is helpful in Minimal Intervention Dentistry because it releases fluoride ions and is highly biocompatible. The aim of this study is to investigate the mechanisms by which hydroxyapatite (HAp) improves the mechanical strength and bioactive functioning of GIC when these materials are combined to make apatite ionomer cement (AIC). A conventional GIC powder was mixed with porous, spherical-HAp particles (HApS), crystalline HAp (HAp200) or one of two types of cellulose. The micro-compressive strengths of the additive particles were measured, and various specimens were evaluated with regard to their compressive strengths (CS), fluoride release concentrations (fluoride electrode) and multi-element release concentrations. The AIC was found to release higher concentrations of fluoride (1.2 times) and strontium ions (1.5 times) compared to the control GIC. It was detected the more release of calcium originated from HApS than HAp200 in AIC. The CS of the AIC incorporating an optimum level of HAp was also significantly higher than that of the GIC. These results suggest that adding HAp can increase the release concentration of ions required for remineralization while maintaining the CS of the GIC. This effect does not result from a physical phenomenon, but rather from chemical reactions between the HAp and polyacrylic acid of GIC.

The purpose of this study was to examine the anti-oral microorganism effects of fluorine and/or silver ions implanted into acrylic resin (PMMA) using plasma-based ion implantation (PBII) with argon gas. The experimental PMMA specimens were implanted with F and Ag ions alone or simultaneously by the PBII method using Ar or Ar/F₂ gases and Ag mesh. The surface characteristics were evaluated by X-ray photoelectron spectroscopy (XPS), contact angle measurements, and atomic force microscopy (AFM). Moreover, the antibacterial activity against Streptococcus mutans (S. mutans) and the antifungal activity against Candida albicans (C. albicans) were examined by the adenosine-5’-triphosphate (ATP) emission luminescence method. XPS spectra of the modified specimens revealed peaks due to F in the Ar/F and the Ar/F+Ag groups, and due to Ag in the Ar+Ag and the Ar/F+Ag groups. The water contact angle increased significantly due to the implantation of Ar, F, and Ag. In the AFM observations, the surface roughness of the Ar/F and the Ar/F+Ag groups increased significantly by less than 5 nanometers. The presence of F and Ag was found to inhibit S. mutans growth in the Ar+Ag and the Ar/F+Ag groups. However, this method provided no significant antifungal activity against C. albicans.