A hardwood, Eucalyptus globulus Labill., and a softwood Pinus pinaster Aiton., were heat treated at temperatures between 170 and 210ºC in an oven and in an autoclave. The samples were pre-extracted with dichloromethane, ethanol and water and ground prior to Fourier Transform Infrared (FTIR) spectroscopic analysis.The heat treatment caused significant changes in the chemical composition and structure of wood, in lignin and polysaccharides. Hemicelluloses were the first to degrade as proved by the initial decrease of the 1730 cm-1 peak due to the breaking of acetyl groups in xylan. Hardwood lignin changed more than softwood lignin, with a shift of maximum absorption from 1505 cm-1 to approximately 1512 cm-1 due to decrease of methoxyl groups, loss of syringyl units or breaking of aliphatic side-chains. The macromolecular structure becomes more condensed and there is a clear increase of non-conjugated (1740 cm-1) in relation to conjugated groups (1650 cm-1). However, the changes induced by the thermal treatment are difficult to monitor by FTIR spectroscopy due to the different chemical reactions occurring simultaneously.

The cultivation of walnut (Juglans regiaL.) for the exploitation of the fruit has been increasingly recognized worldwide; therefore, it is important to valorize a large amount of biomass from walnut shells (WS), where liquefaction may play an important role. This work intends to contribute to an improved understanding of the best uses for this material. The assays were made with a binary mixture of ethylene glycol and glycerol (1:1 v/v) as solvents, catalyzed by sulfuric acid. The tested parameters were as follows: particle size >0.420–0.177 mm, temperature 140–200°C, and reaction time between 15 and 60 min. The initial dried material, the liquefied material, and the resulting solid residue were analyzed by FTIR-ATR for polyol characterization. The results showed that WS are mostly composed of lignin with 35.0% and polysaccharides, 30.0% cellulose and 24.9% hemicelluloses. High-lignin content indicated that WS might be used as a bio-fuel or adhesives. Extractives represent 10.2% with almost half (4.6%) of polar extractives. The best conditions to attain the optimal liquefaction yield were 160°C, 30 min, and 0.420–0.250 mm particle size, for the tested parameters. FTIR spectrum of the liquefied material is very different from the original material, and solid residue spectra seem to indicate that there is higher liquefaction of polysaccharides when compared with lignin since there is a higher absorption at 1,600 cm⁻¹and lower absorption at 1,040 cm⁻¹and that liquefied compounds are probably in smaller molecules.

The introduction of new species in forest management must be undertaken with a degree of care, to help prevent the spread of invasive species. However, new species with higher profitability are needed to increase forest products value and the resilience of rural populations. Paulownia tomentosa has an extremely fast growth. The objective and novelty of this work was to study the potential use of young Paulownia trees grown in Portugal by using heat treatment to improve its properties, thereby allowing higher value applications of the wood. The average chemical composition of untreated and heat-treated wood was determined. The extractive content was determined by successive Soxhlet extraction with dichloromethane (DCM), ethanol and water as solvents. The composition of lipophilic extracts was performed by injection in GC-MS with mass detection. Insoluble and soluble lignin, holocellulose and α-cellulose were also determined. Physical (density and water absorption and dimensional stability) and mechanical properties (bending strength and bending stiffness) and termite resistance was also determined. Results showed that extractive content increased in all solvents, lignin and α-cellulose also increased and hemicelluloses decreased. Compounds derived from the thermal degradation of lignin were found in heat-treated wood extractions. Dimensional stability improved but there was a decrease in mechanical properties. Resistance against termites was better for untreated wood than for heat-treated wood, possibly due to the thermal degradation of some toxic extractives.