An arrangement of self-assembled GaN nanowires (NWs) grown by plasma-assisted molecular beam epitaxy on a Si(111) substrate is studied as a function of the temperature at which the substrate is nitridized before GaN growth. We show that the NWs grow with the c-axis perpendicular to the substrate surface independently of nitridation temperature with only a slight improvement in tilt coherency for high nitridation temperatures. A much larger influence of the substrate nitridation process on the in-plane arrangement of NWs is found. For high (850 °C) and medium (450 °C) nitridation temperatures angular twist distributions are relatively narrow and NWs are epitaxially aligned to the substrate in the same way as commonly observed in GaN on Si(111) planar layers with an AlN buffer. However, if the substrate is nitridized at low temperature (~150 °C) the epitaxial relationship with the substrate is lost and an almost random in-plane orientation of GaN NWs is observed. These results are correlated with a microstructure of silicon nitride film created on the substrate as the result of the nitridation procedure.

Nucleation kinetics of GaN nanowires (NWs) by molecular beam epitaxy on amorphous AlxOy buffers deposited at low temperature by atomic layer deposition is analyzed. We found that the growth processes on a-AlxOy are very similar to those observed on standard Si(111) substrates, although the presence of the buffer significantly enhances nucleation rate of GaN NWs, which we attribute to a microstructure of the buffer. The nucleation rate was studied vs. the growth temperature in the range of 720–790 °C, which allowed determination of nucleation energy of the NWs on a-AlxOy equal to 6 eV. This value is smaller than 10.2 eV we found under the same conditions on nitridized Si(111) substrates. Optical properties of GaN NWs on a-AlxOy are analyzed as a function of the growth temperature and compared with those on Si(111) substrates. A significant increase of photoluminescence intensity and much longer PL decay times, close to those on silicon substrates, are found for NWs grown at the highest temperature proving their high quality. The samples grown at high temperature have very narrow PL lines. This allowed observation that positions of donor-bound exciton PL line in the NWs grown on a-AlxOy are regularly lower than in samples grown directly on silicon suggesting that oxygen, instead of silicon, is the dominant donor. Moreover, PL spectra suggest that total concentration of donors in GaN NWs grown on a-AlxOy is lower than in those grown under similar conditions on bare Si. This shows that the a-AlxOy buffer efficiently acts as a barrier preventing uptake of silicon from the substrate to GaN.

We present a comprehensive description of the self-assembled nucleation and growth of GaN nanowires (NWs) by plasma-assisted molecular beam epitaxy on amorphous Al _x O _y buffers (a-Al _x O _y ) prepared by atomic layer deposition. The results are compared with those obtained on nitridated Si(111). Using line-of-sight quadrupole mass spectrometry, we analyze in situ the incorporation of Ga starting from the incubation and nucleation stages till the formation of the final nanowire ensemble and observe qualitatively the same time dependence for the two types of substrates. However, on a-Al _x O _y the incubation time is shorter and the nucleation faster than on nitridated Si. Moreover, on a-Al _x O _y we observe a novel effect of decrease in incorporated Ga flux for long growth durations which we explain by coalescence of NWs leading to reduction of the GaN surface area where Ga may reside. Dedicated samples are used to analyze the evolution of surface morphology. In particular, no GaN nuclei are detected when growth is interrupted during the incubation stage. Moreover, for a-Al _x O _y , the same shape transition from spherical cap-shaped GaN crystallites to the NW-like geometry is found as it is known for nitridated Si. However, while the critical radius for this transition is only slightly larger for a-Al _x O _y than for nitridated Si, the critical height is more than six times larger for a-Al _x O _y . Finally, we observe that in fully developed NW ensembles, the substrate no longer influences growth kinetics and the same N-limited axial growth rate is measured on both substrates. We conclude that the same nucleation and growth processes take place on a-Al _x O _y as on nitridated Si and that these processes are of a general nature. Quantitatively, nucleation proceeds somewhat differently, which indicates the influence of the substrate, but once shadowing limits growth processes to the upper part of the NW ensemble, they are not affected anymore by the type of substrate.