The main aim of this article is the analysis of the deformation process of regular cell structures under quasi-static load conditions. The methodology used in the presented investigations included a manufacturability study, strength tests of the base material as well as experimental and numerical compression tests of developed regular cellular structures. A regular honeycomb and four variants with gradually changing topologies of different relative density values have been successfully designed and produced in the TPU-Polyflex flexible thermoplastic polyurethane material using the Fused Filament Fabrication (FFF) 3D printing technique. Based on the results of performed technological studies, the most productive and accurate 3D printing parameters for the thermoplastic polyurethane filament were defined. It has been found that the 3D printed Polyflex material is characterised by a very high flexibility (elongation up to 380%) and a non-linear stress-strain relationship. A detailed analysis of the compression process of the structure specimens revealed that buckling and bending were the main mechanisms responsible for the deformation of developed structures. The Finite Element (FE) method and Ls Dyna software were used to conduct computer simulations reflecting the mechanical response of the structural specimens subjected to a quasi-static compression load. The hyperelastic properties of the TPU material were described with the Simplified Rubber Material (SRM) constitutive model. The proposed FE models, as well as assumed initial boundary conditions, were successfully validated. The results obtained from computer simulations agreed well with the data from the experimental compression tests. A linear relationship was found between the relative density and the maximum strain energy value.

Advances in the development of additive manufacturing materials (AM) and the low availability of studies on the impact response of AM specimens are the main reasons for this paper. Therefore, the influence of building orientation (vertical and horizontal) and the angle of the raster (15°/−75°, 30°/−60°, 45°/−45°, and 0°/90°) on the tensile and impact strength of AM specimens was investigated. The polylactic acid (PLA)-PolyMax, Mediflex and acrylonitrile-butadiene-styrene (ABS) filaments were chosen to provide a comprehensive characterization of AM materials with versatile mechanical properties. The experimental results of this study show that the tensile strength and toughness of PolyMax PLA specimens are comparable to ABS specimens, while Mediflex samples are characterized by their higher toughness, but lower impact force needed to break the samples. The Mediflex Charpy fracture surfaces exhibit a ductile character compared to those of brittle ABS and PLA. Furthermore, fracture surface morphology shows the allocation of voids, which helps us to understand differences in mechanical properties, and allows one to properly interpret the results of the geometrical accuracy of AM specimens with various printing settings.

Growth in the development of additive manufacturing materials (AM) and the low availability of studies on the impact response of AM specimens is the main reason for this paper. Therefore, the influence of the building orientation (vertical and horizontal) and the angle of the raster (15°/-75°, 30°/-60°, 45°/-45°, and 0°/90°) on the tensile and impact strength of the AM specimens was investigated. The PLA PolyMax, Mediflex and ABS filaments were chosen to provide comprehensive characterization for AM materials with versatile mechanical properties. The experimental results of this study show that the tensile strength and toughness of PolyMax PLA specimens are comparable to ABS specimens while Mediflex samples are characterized with higher toughness but lower impact force needed to break the samples. The Mediflex Charpy fracture surfaces exhibit ductile character compared to those of brittle ABS and PLA. Furthermore, fracture surface morphology shows the allocation of voids which helps to understand differences in mechanical properties and allows one to properly interpret the results of geometrical accuracy of AM specimens with various printing settings.

This paper presents the results of preliminary tests on specimens made from mixtures of dendritic copper powder (CuE) with the graphene-coated copper powder (CuG) in a range from 20% to 100% (CuG). The properties of the powder mixtures, green compacts and sinters were determined. To study the properties of the powder mixtures, the following tests were carried out: a measurement of the CuG powder grain size after the grinding process, measurements of the bulk density and tap density of the prepared powder mixtures. The porosity of the produced green compacts and the sinters was calculated as well as the densification capabilities of the powder mixtures by die pressing, cold isostatic pressing and sintering in a reducing atmosphere were tested. Moreover, the nature of the porosity formation was analysed using an optical microscope and the Brinell hardness was determined. The measured Brinell hardness was in the range of 17 HB for sinters made from CuG to 34 HB for sinters made from a 20% CuG powder mixture. More than six hundred measurements that were made in this study show that the high CuG content in the powder mixture reduce the hardness of the sinters as well increase their porosity.