This paper presents the characteristic of 316L steel turning obtained by 3D printing. The analysis of the influence of turning data on the components of the total cutting force, surface roughness and the maximum temperature values in the cutting zone are presented. The form of chips obtained in the machining process was also analyzed. Statistical analysis of the test results was developed using the Taguchi method.

This article presents selected issues related to the workpiece surface quality after machining by the laser sintering of AlSi10MG alloy powder. The surfaces of the workpiece were prepared and machined by longitudinal turning with tools made of sintered carbides. The occurrence of breaches on the machined material surface was found, which negatively influence the values of 3D surface roughness parameters. The occurring phenomena were analyzed and proposals for their explanation were made. Guidelines for the machining of workpieces achieved by the laser sintering of powders were developed. The lowest value of the 3D roughness parameters was obtained for f = 0.06 mm/rev, a_p = 0.5–1.0 mm, and for the nose radius of cutting insert r_ε = 0.8 mm. The results of research on the effect of cutting parameters on the values of parameters describing the surface quality are presented. Topography measurements and 3D surface roughness parameters are presented, as well as the results of a microscopic 3D surface analysis. Taguchi’s method was used in the research methodology.

In the machining of difficult-to-cut alloys, such as titanium-based alloys, the delivery of a cutting fluid with high pressure can increase machining efficiency and improve process stability through more efficient chip breaking and removing. Proper selection of machining conditions can increase the productivity of the process while minimizing production costs. To present the influence of cutting fluid pressure and chip breaker geometry on the chip breaking process for various chip cross-sections Grade 5 ELI titanium alloy turning tests were carried out using carbide tools, H13A grade, with a -SF chip breaker geometry under the cutting fluid pressure of 70 bar. Measurements of the total cutting force components for different cutting speeds, feeds, and cutting depth in finishing turning were carried out. The analysis of the obtained chips forms and the application area of the chip breaker have been presented. It was proved that for small depth of cut (leading to small chip cross-section) the cutting fluid pressure is the main cause of the chip breakage, since the insert chip breaker does not work. On the other hand, for bigger depths of cut where the chip breaker goes in action, the cutting fluid pressure only supports this process. For medium values of depths of cut the strength of chip is high enough so that the pressure of the cutting fluid cannot cause chip breaking. A chip groove is not filled completely so the chip breaker cannot play its role.

This article presents investigations related to the turning of stainless steel as a representative of difficult-to-cut materials and the effectiveness of selected chip breakers working in the local machining environment. Martensitic steel AISI 416 was used to test two commercially available types of chip breaker. The efficiency of a chip breaker working in the range of cutting conditions recommended (by the tool manufacturers) was the aim of the turning tests. As a result of the investigations an algorithm of cutting condition selection, combining both the cutting tests and the simulation procedure for the efficiency of the chip breaker was created. The vision system, equipped with a high-speed camera was used for chip form estimation. Simultaneously, the cutting force components were measured to check if the simulation calculation was correct. The FEM simulation was applied to estimate the manner in which the chip groove was filled. The article presents certain recommendations for cutting condition correction in the local machining environment for the purpose of achieving an acceptable chip form.

This article describes issues related to the machining of parts made of sintered nickel-cobalt alloy. Longitudinal turning with a CBN (cubic boron nitride) tool was analyzed. The results of experiments showed the influence of cutting parameters in the field of finishing machining on the values of cutting forces and specific cutting force, taking into account the wear of the cutting edge. Measurements and analysis of the topography and roughness parameters of the machined surface, as well as the cutting tool wear, were presented. The microscopic examination showed that the average grain size of the sintered nickel-cobalt alloy was 3.22 ± 0.1 (μm). The presence of the hardening state variability of the material during machining, as well as the value of the cutting force fluctuation as a function of the tool wear VB, were stated. The specific cutting force values increased to a small degree for the tool wear in the range of VB = 0–0.2 mm, and reached similar values in the range k_c = 5500–7500 N/mm². The specific cutting force values increased significantly for wear VB > 0.2 mm and were characterized by a large variability. The occurring phenomena were analyzed and several explanations were proposed. A recommendation was developed for the machining of parts made of sintered nickel-cobalt alloy. The Taguchi method was used in the experiment methodology.