Multiple environmental concerns such as garbage generation, accumulation in disposal systems and recyclability are powerful drivers for the use of many biodegradable materials. Due to the new uses and requests of plastic users, the consumption of biopolymers is increasing day by day. Polylactic Acid (PLA) being one of the most promising biopolymers and researched extensively, it is emerging as a substitute for petroleum-based polymers. Similarly, owing to both environmental and economic benefits, as well as to their technical features, natural fibers are arising as likely replacements to synthetic fibers to reinforce composites for numerous products. This work reviews the current state of the art of PLA compounds reinforced with two of the high strength natural fibers for this application: flax and jute. Flax fibers are the most valuable bast-type fibers and jute is a widely available plant at an economic price across the entire Asian continent. The physical and chemical treatments of the fibers and the production processing of the green composites are exposed before reporting the main achievements of these materials for structural applications. Detailed information is summarized to understand the advances throughout the last decade and to settle the basis of the next generation of flax/jute reinforced PLA composites (200 Maximum).

Quest for producing lightweight and biodegradable materials has encouraged researchers to replace synthetic fibers with natural fibers. Hence a study is made to investigate the effects of introducing secondary reinforcement (natural fibers), stacking sequence, and addition of graphite particles on the mechanical characteristics and water uptakes along with diffusivity of hybrid (glass\jute) composites. Different weight fractions of graphite particulates are incorporated into the epoxy to produce different samples having 4 plies for each sample by hand layup vacuum bagging method. The obtained specimens are subjected to various mechanical tests, water absorption tests as per the ASTM standards, and optical microscopy was used to study the fracture morphology of the samples. The results displayed that the properties are deteriorated a little with the addition of secondary reinforcement, however they have improved with the addition of graphite. E-Glass as skin layer and treated jute as core layer composite exhibits ameliorate tensile strength (201.5 MPa), compression strength (515.12 MPa), flexural strength (106.9 MPa), hardness (25 BHN). However highest impact energy of 26 J is recorded for the sample with jute as skin layer and E-Glass as the core layer. Water absorption tests revealed that the addition of graphite has reduced the water absorption in the hybrid samples.

Different types of heating systems have been developed lately, representing a growing interest in both the academic and industrial sectors. Based on the Joule effect, fibrous structures can produce heat once an electrical current is passed, whereby different approaches have been followed. For that purpose, materials with electrical and thermal conductivity have been explored, such as carbon-based nanomaterials, metallic nanostructures, intrinsically conducting polymers, fibers or hybrids. We review the usage of these emerging nanomaterials at the nanoscale and processed up to the macroscale to create heaters. In addition to fibrous systems, the creation of composite systems for electrical and thermal conductivity enhancement has also been highly studied. Different techniques can be used to create thin film heaters or heating textiles, as opposed to the conventional textile technologies. The combination of nanoscale and microscale materials gives the best heating performances, and some applications have already been proven, even though some effort is still needed to reach the industry level.

Smart textiles have become a promising area of research for heating applications. Coatings with nanomaterials allow the introduction of different functionalities, enabling doped textiles to be used in sensing and heating applications. These coatings were made on a piece of woven cotton fabric through screen printing, with a different number of layers. To prepare the paste, nanomaterials such as graphene nanoplatelets (GNPs) and multiwall carbon nanotubes (CNTs) were added to a polyurethane-based polymeric resin, in various concentrations. The electrical conductivity of the obtained samples was measured and the heat-dissipating capabilities assessed. The results showed that coatings have induced electrical conductivity and heating capabilities. The highest electrical conductivity of (9.39 ± 1.28 × 10⁻¹ S/m) and (9.02 ± 6.62 × 10⁻² S/m) was observed for 12% (w/v) GNPs and 5% (w/v) (CNTs + GNPs), respectively. The sample with 5% (w/v) (CNTs + GNPs) and 12% (w/v) GNPs exhibited a Joule effect when a voltage of 12 V was applied for 5 min, and a maximum temperature of 42.7 °C and 40.4 °C were achieved, respectively. It can be concluded that higher concentrations of GNPs can be replaced by adding CNTs, still achieving nearly the same performance. These coated textiles can potentially find applications in the area of heating, sensing, and biomedical applications.

Although the force/pressure applied onto a textile substrate through a uniaxial compression is constant and independent of the yarn direction, it should be noted that such mechanical action causes a geometric change in the substrate, which can be identified by the reduction in its lateral thickness. Therefore, the objective of this study was to investigate the influence of the fabric orientation on both knitted and woven pressure sensors, in order to generate knowledge for a better design process during textile piezoresistive sensor development. For this purpose, these distinct textile structures were doped with different concentrations of graphene nanoplatelets (GNPs), using the screen-printing technique. The chemical and physical properties of these screen-printed fabrics were analysed using Field Emission Scanning Electron Microscopy, Ground State Diffuse Reflectance and Raman Spectroscopy. Samples were subjected to tests determining linear electrical surface resistance and piezoresistive behaviour. In the results, a higher presence of conductive material was found in woven structures. For the doped samples, the electrical resistance varied between 10⁵ Ω and 10¹ Ω, for the GNPs’ percentage increase. The lowest resistance value was observed for the woven fabric with 15% GNPs (3.67 ± 8.17 × 10¹ Ω). The samples showed different electrical behaviour according to the fabric orientation. Overall, greater sensitivity in the longitudinal direction and a lower coefficient of variation CV% of the measurement was identified in the transversal direction, coursewise for knitted and weftwise for woven fabrics. The woven fabric doped with 5% GNPs assembled in the weftwise direction was shown to be the most indicated for a piezoresistive sensor, due to its most uniform response and most accurate measure of mechanical stress.