A novel high silicon austempered (AHS) steel has been studied in this work. The effect of different austenitizing temperatures, in full austenitic and biphasic regime, on the final microstructure was investigated. Specimens were austenitized at 780 °C, 830 °C, 850 °C and 900 °C for 30 min and held isothermally at 350 °C for 30 min. A second heat treatment route was performed which consisted of austenitizing at 900 °C for 30 min and austempering at 300 °C, 350 °C and 400 °C for 30 min. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) have been used to evaluate the microstructural evolution. These techniques revealed that the microstructures were composed of carbide-free bainite, ferrite, martensite and retained austenite (RA) in different volume fractions (Vγ). An aqueous borate buffer solution with 0.3 M H₃BO₃ and 0.075 M Na₂B₄O₇∂10H₂O (pH = 8.4) was used for corrosion tests in order to evaluate the influence of the different volume fractions of retained austenite on the corrosion properties of the specimens. The results showed that when increasing the austenitization temperatures, the volume fractions of retained austenite reached a maximum value at 850 °C, and decrease at higher temperatures. The corrosion properties were investigated after 30 min and 24 h immersion by means of potentiodynamic polarization (after 30 min) and electrochemical impedance spectroscopy (after both 30 min and 24 h) tests. The corrosion resistance of the samples increased with increases in the volume fraction of retained austenite due to lower amounts of residual stresses.

High Silicon Austempered steels (AHSS) are materials of great interest due to their excellent combination of high strength, ductility, toughness, and limited costs. These steel grades are characterized by a microstructure consisting of ferrite and bainite, accompanied by a high quantity retained austenite (RA). The aim of this study is to analyze the effect of an innovative heat treatment, consisting of intercritical annealing at 780 °C and austempering at 400 °C for 30 min, on the microstructure and mechanical properties of a novel high silicon steel (0.43C-3.26Si-2.72Mn wt.%). The microstructure was characterized by optical and electron microscopy and XRD analysis. Hardness and tensile tests were performed. A multiphase ferritic-martensitic microstructure was obtained. A hardness of 426 HV and a tensile strength of 1650 MPa were measured, with an elongation of 4.5%. The results were compared with those ones obtained with annealing and Q&T treatments.