Poly(methyl methacralyate) (PMMA) has long been used in dentistry as a base polymer for dentures, and it is recently being used for the 3D printing of dental materials. Despite its many advantages, its susceptibility to microbial colonization remains to be overcome. In this study, the interface between 3D-printed PMMA specimens and oral salivary biofilm was studied following the addition of zwitterionic materials, 2-methacryloyloxyethyl phosphorylcholine (MPC) or sulfobetaine methacrylate (SB). A significant reduction in bacterial and biofilm adhesions was observed following the addition of MPC or SB, owing to their protein-repellent properties, and there were no significant differences between the two test materials. Although the mechanical properties of the tested materials were degraded, the statistical value of the reduction was minimal and all the properties fulfilled the requirements set by the International Standard, ISO 20795-2. Additionally, both the test materials maintained their resistance to biofilm when subjected to hydrothermal fatigue, with no further deterioration of the mechanical properties. Thus, novel 3D-printable PMMA incorporated with MPC or SB shows durable oral salivary biofilm resistance with maintenance of the physical and mechanical properties.

The increasing demand for orthodontic treatment over recent years has led to a growing need for the retrieval and reuse of titanium-based miniscrews to reduce the cost of treatment, especially in patients with early treatment failure due to insufficient primary stability. This in vitro study aimed to evaluate differences in the primary stability between initially inserted and re-inserted miniscrews within different cortical bone densities. Artificial bone was used to simulate cortical bone of different densities, namely 20, 30, 40, and 50 pound per cubic foot (pcf), where primary stability was evaluated based on maximum insertion torque (MIT), maximum removal torque (MRT), horizontal resistance, and micromotion. Scanning electron microscopy was used to evaluate morphological changes in the retrieved miniscrews. The MIT, MRT, horizontal resistance, and micromotion was better in samples with higher cortical bone density, thereby indicating better primary stability (P < 0.05). Furthermore, a significant reduction of MIT, MRT, and horizontal resistance was observed during re-insertion compared with the initial insertion, especially in the higher density cortical bone groups. However, there was no significant change in micromotion. While higher cortical bone density led to better primary stability, it also caused more abrasion to the miniscrews, thereby decreasing the primary stability during re-insertion.

Miniscrews have gained recent popularity as temporary anchorage devices in orthodontic treatments, where failure due to sinus perforations or damage to the neighboring roots have increased. Issues regarding miniscrews in insufficient interradicular space must also be resolved. This study aimed to evaluate the primary stability of miniscrews shorter than 6 mm and their feasibility in artificial bone with densities of 30, 40, and 50 pounds per cubic foot (pcf). The primary stability was evaluated by adjusting the intrabony miniscrew length, based on several physical properties: maximum insertion torque (MIT), maximum removal torque (MRT), removal angular momentum (RAM), horizontal resistance, and micromotion. The MIT and micromotion results demonstrated that the intrabony length of a miniscrew significantly affected its stability in low-density cortical bone, unlike cases with a higher cortical bone density (p < 0.05). The horizontal resistance, MRT, and RAM were affected by the intrabony length, regardless of the bone density (p < 0.05). Thus, the primary stability of miniscrews was affected by both the cortical bone density and intrabony length. The effect of the intrabony length was more significant in low-density cortical bone, where the implantation depth increased as more energy was required to remove the miniscrew. This facilitated higher resistance and a lower risk of falling out.