Metal additive manufacturing processes often use gas-atomized powder as feedstock, but these processes use different methods for consolidation. Depending on the consolidation temperature, secondary phases may be retained during processing, making it important to understand powder microstructure prior to consolidation. Commercial alloy compositions are typically used for these powders because they have been widely studied and qualified; however, the microstructure of the powder form of these compositions has not been studied. This paper aims to understand the commercial Al 6061 powder: how the internal microstructure of the powder differs from wrought both in the as-manufactured and thermally-treated conditions. A specific focus is put on the Mg-rich phases and their morphologies. This was accomplished through transmission electron microscopy, scanning transmission electron microscopy, and energy dispersive x-ray spectroscopy. Both the size and morphology of the phases in the powder differ greatly from those in the wrought form.

Al 7075 is a heat-treatable Al–Mg–Zn alloy widely used in the aerospace industry. Recently, it has found application as feedstock for metal additive manufacturing (MAM). It has been shown that wrought alloy compositions in powder form differ in microstructure and properties from their conventional form. Given this, it is important to understand the microstructure of the powders prior to use in MAM processes. This work studies as-atomized gas-atomized Al 7075 powders and the effect of thermal treatments on microstructure. Extensive electron microscopy revealed the presence of T-phase, Al₇Cu₂Fe, and Mg₂Si in the as-atomized condition. Thermal treatments were performed at 465 °C and 480 °C to homogenize the microstructure; however, S-phase was unexpectedly present in the samples treated at 465 °C. In both 465 °C and 480 °C treatments, T-phase was not fully dissolved after the 60-min treatment. Guided by thermodynamic modeling, these results indicate a shift in local equilibria in these powders.