This paper focuses on the microstructure, phase composition, mechanical, tribological and corrosion properties of high-entropy alloys (HEAs) in the CoCrCuFeNi system depending on copper content, which was varied from 0 to 20 at. % with an increment of 5%. CoCrCuFeNi alloys were manufactured by powder metallurgy methods: mechanical alloying and hot pressing of element mixtures. The solubility limit of copper in CoCrFeNi solid solution was found to be 9 at. %. Segregation of irregularly shaped copper grains sized 1–30 μm is observed at concentrations above this solubility limit. As copper concentration increases, the phase composition of CoCrCuFeNi alloys changes from the single phase based on FCC1 solid solution (Cu = 0–5 at. %) to the dual-phase FCC1 + FCC2 alloy (Cu = 10–20 at. %), where FCC1 is the main phase and FCC2 is the secondary copper-rich phase. Tribological tests have shown that doping the CoCrFeNi alloy with copper increased wear resistance by 23% due to solid solution hardening. As copper content rises above 20%, the content of the secondary FCC2 phase increases, while wear resistance and alloy hardness decline. An analysis of wear tracks and wear products has shown that abrasion of CoCrCuFeNi alloys occurs via the abrasive-oxidative wear mechanism. The corrosion tests of CoCrCuFeNi HEAs in 3.5% NaCl solution had demonstrated that doping the alloy with copper at low concentrations (5–10%) leads to decreasing of corrosion resistance, possibly due to the formation of undesirable oxide Cu₂O along with protective Cr₂O₃. At high copper concentrations (15–20%) galvanic corrosion is suppressed due to coarsening of FCC2 grains and thus decreasing the specific contact surface area between the cathode (FCC2) and the anode (FCC1).

Co- and Fe-based alloys produced by powder technology are being widely used as a matrix for diamond-containing composites in cutting, drilling, grinding pplications, etc. The severe service conditions demand that the mechanical and tribological properties of these alloys be improved. Development of metal-matrix composites (MMCs) and alloys reinforced with nanoparticles is a promising way to resolve this problem. In this work, we have investigated the effect of nano-sized WC, ZrO₂, Al₂O₃, and Si₃N₄ additives on the properties of sintered dispersion-strengthened Co- and Fe-based MMCs. The results show an increase in the hardness (up to 10 HRB), bending strength (up to 50%), wear resistance (by a factor of 2–10) and a decrease in the friction coefficient (up to 4-fold) of the dispersion-strengthened materials. The use of designed alloys as a binder of cutting diamond tools gave a 4-fold increment in the service life, without reduction in their cutting speed.

The state of the art of the studies in the field of the development and certification of novel multifunctional nanostructured coatings having a wide spectrum of applications is reviewed. The main...

Compact ceramic materials based on the M n + 1AX nphases in the Ti-Cr-Al-C system are produced by forced self-propagating high-temperature synthesis (SHS) compaction. The mechanisms of the structure...

Macrokinetic characteristics of the combustion of mixtures in the (100% − X)(Ti + 0.5C) + X(Ta + C) system with a variable mixing parameter X and initial temperature T ₀ of charge heating are considered. For compositions with X = 10 and 30%, an abrupt increase in the velocity U _c and temperature T _c of combustion as a result of passing two parallel chemical reactions of titanium and tantalum carbide formation is established. The U _c (T ₀) and T _c (T ₀) dependencies are linear for the mixture with X = 50%. By hardening the combustion wave, it is revealed that the primary structure formation in the combustion region starts from the selection of submicron grains of nonstoichiometric titanium carbide from the supersaturated titanium melt. In the investigated range of parameter X, synthetic products are single-phase and represent titanium-tantalum carbide. An increase in X results in a decrease in the size and microhardness of (Ti, Ta) C grains and a reduction of the relative density of compact synthetic products. The kinetics of high-temperature oxidation of alloys on the basis of carbide (Ti, Ta) C is studied. Ceramics produced at X = 10% are most heat-resistant.