This paper focuses on the microstructure, phase composition, mechanical, tribological and corrosion properties of high-entropy alloys (HEAs) in the CoCrCuFeNi system depending on copper content, which was varied from 0 to 20 at. % with an increment of 5%. CoCrCuFeNi alloys were manufactured by powder metallurgy methods: mechanical alloying and hot pressing of element mixtures. The solubility limit of copper in CoCrFeNi solid solution was found to be 9 at. %. Segregation of irregularly shaped copper grains sized 1–30 μm is observed at concentrations above this solubility limit. As copper concentration increases, the phase composition of CoCrCuFeNi alloys changes from the single phase based on FCC1 solid solution (Cu = 0–5 at. %) to the dual-phase FCC1 + FCC2 alloy (Cu = 10–20 at. %), where FCC1 is the main phase and FCC2 is the secondary copper-rich phase. Tribological tests have shown that doping the CoCrFeNi alloy with copper increased wear resistance by 23% due to solid solution hardening. As copper content rises above 20%, the content of the secondary FCC2 phase increases, while wear resistance and alloy hardness decline. An analysis of wear tracks and wear products has shown that abrasion of CoCrCuFeNi alloys occurs via the abrasive-oxidative wear mechanism. The corrosion tests of CoCrCuFeNi HEAs in 3.5% NaCl solution had demonstrated that doping the alloy with copper at low concentrations (5–10%) leads to decreasing of corrosion resistance, possibly due to the formation of undesirable oxide Cu₂O along with protective Cr₂O₃. At high copper concentrations (15–20%) galvanic corrosion is suppressed due to coarsening of FCC2 grains and thus decreasing the specific contact surface area between the cathode (FCC2) and the anode (FCC1).

Coatings in a Zr-Mo-Si-B-N system were deposited by the magnetron sputtering of ZrB₂-MoSi₂ targets in argon and nitrogen. The structure of the coatings was investigated using scanning electron microscopy, X-ray diffraction, energy-dispersive spectroscopy, and glow-discharge optical emission spectroscopy. Mechanical and tribological properties were measured using nanoindentation and pin-on-disc testing. Oxidation resistance and oxidation kinetics were estimated via annealing in air at 1000–1500 °C and precision weight measurements. We found that the coatings deposited in Ar demonstrate a superior combination of properties, including hardness of 36 GPa, elastic recovery of 84%, a friction coefficient of 0.6, and oxidation resistance at temperatures up to 1200 °C. High oxidation resistance is realized due to the formation of the protective (SiO₂ + ZrO₂)/SiO₂ oxide layer, which inhibits the diffusion of oxygen into the coating.