Chitosan/bacterial cellulose composite films containing diamond nanoparticles (NDs) with potential application as wound dressing are introduced. Microstructural studies show that NDs are uniformly dispersed in the matrix, although slight agglomeration at concentrations above 2 wt % is seen. Fourier transform infrared spectroscopy reveals formation of hydrogen bonds between NDs and the polymer matrix. X-ray diffraction analysis indicates reduced crystallinity of the polymer matrix in the presence of NDs. Approximately 3.5-fold increase in the elastic modulus of the composite film is obtained by the addition of 2 wt % NDs. The results of colorimetric analysis show that the composite films are transparent but turn to gray-like and semitransparent at high ND concentrations. Additionally, a decrease in highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) gap is also seen, which results in a red shift and higher absorption intensity towards the visible region. Mitochondrial activity assay using L929 fibroblast cells shows that the nanocomposite films are biocompatible (>90%) after 24 h incubation. Multiple lamellapodia and cell-cell interaction are shown. The results suggest that the developed films can potentially be used as a flexible platform for wound dressing.

Biodegradable polymer nanocomposites (BPNCs) are advanced materials that have gained significant attention over the past 20 years due to their advantages over conventional polymers. BPNCs are eco-friendly, cost-effective, contamination-resistant, and tailorable for specific applications. Nevertheless, their usage is limited due to their unsatisfactory physical and mechanical properties. To improve these properties, nanofillers are incorporated into natural polymer matrices, to enhance mechanical durability, biodegradability, electrical conductivity, dielectric, and thermal properties. Despite the significant advances in the development of BPNCs over the last decades, our understanding of their dielectric, thermal, and electrical conductivity is still far from complete. This review paper aims to provide comprehensive insights into the fundamental principles behind these properties, the main synthesis, and characterization methods, and their functionality and performance. Moreover, the role of nanofillers in strength, permeability, thermal stability, biodegradability, heat transport, and electrical conductivity is discussed. Additionally, the paper explores the applications, challenges, and opportunities of BPNCs for electronic devices, thermal management, and food packaging. Finally, this paper highlights the benefits of BPNCs as biodegradable and biodecomposable functional materials to replace traditional plastics. Finally, the contemporary industrial advances based on an overview of the main stakeholders and recently commercialized products are addressed.

Magnesium-based implants (MBIs) have recently attracted great attention in bone regeneration due to elastic modulus similar to bone. Nevertheless, the degradation rate and hydrogen release of MBIs in the body have to be tackled for practical applications. In the present study, we present a metal–organic framework (MOF) nanoplates to reduce the degradation rate of AZ91 magnesium alloy. Zeolitic imidazolate frameworks (ZIF-8) with a specific surface area of 1789 m² g⁻¹ were prepared by solvothermal methods, and after dispersion in a chitosan solution (10% w/w), the suspension was electrospun on the surface of AZ91 alloy. Studying the degradation rate in simulated body fluid (SBF) by electrochemical analysis including potentiodynamic polarization and electrochemical impedance spectroscopy reveals that the degradation rate of the surface-modified implants decreases by ~ 80% as compared with the unmodified specimens. The reduced alkalization of the physiological environment and hydrogen release due to the implant degradation are shown. In vitro studies by fibroblasts and MG63 osteosarcoma cells exhibit improved cell adhesion and viability. The mechanisms behind the improved degradation resistance and enhanced bioactivity are presented and discussed. Surface modification of MBIs by MOF-chitosan coatings is a promising strategy to control the biodegradation of magnesium implants for bone regeneration.

Cardiac troponin-I (cTnI) is a well-known biomarker for the diagnosis and control of acute myocardial infarction in clinical practice. To improve the accuracy and reliability of cTnI electrochemical immunosensors, we propose a multilayer nanostructure consisting of Fe₃O₄-COOH labeled anti-cTnI monoclonal antibody (Fe₃O₄-COOH-Ab₁) and anti-cTnI polyclonal antibody (Ab₂) conjugated on Au-Ag nanoparticles (NPs) decorated on a metal–organic framework (Au-Ag@ZIF-67-Ab₂). In this design, Fe₃O₄-COOH was used for separation of cTnI in specimens and signal amplification, hierarchical porous ZIF-67 extremely enhanced the specific surface area, and Au-Ag NPs synergically promoted the conductivity and sensitivity. They were additionally employed as an immobilization platform to enhance antibody loading. Electron microscopy images indicated that Ag-Au NPs with an average diameter of 1.9 ± 0.5 nm were uniformly decorated on plate-like ZIF-67 particles (with average size of 690 nm) without any agglomeration. Several electrochemical assays were implemented to precisely evaluate the immunosensor performance. The square wave voltammetry technique exhibited the best performance with a sensitivity of 0.98 mA mL cm⁻² ng⁻¹ and a detection limit of 0.047 pg mL⁻¹ in the linear range of 0.04 to 8 ng mL⁻¹.