The microstructures and mechanical properties of cobalt-chromium (Co-Cr) alloys produced by three CAD/CAM-based processing techniques were investigated in comparison with those produced by the traditional casting technique. Four groups of disc- (microstructures) or dumbbell- (mechanical properties) specimens made of Co-Cr alloys were prepared using casting (CS), milling (ML), selective laser melting (SLM), and milling/post-sintering (ML/PS). For each technique, the corresponding commercial alloy material was used. The microstructures of the specimens were evaluated via X-ray diffractometry, optical and scanning electron microscopy with energy-dispersive X-ray spectroscopy, and electron backscattered diffraction pattern analysis. The mechanical properties were evaluated using a tensile test according to ISO 22674 (n = 6). The microstructure of the alloys was strongly influenced by the manufacturing processes. Overall, the SLM group showed superior mechanical properties, the ML/PS group being nearly comparable. The mechanical properties of the ML group were inferior to those of the CS group. The microstructures and mechanical properties of Co-Cr alloys were greatly dependent on the manufacturing technique as well as the chemical composition. The SLM and ML/PS techniques may be considered promising alternatives to the Co-Cr alloy casting process.

The influence of residual stress induced by sandblasting the zirconia ceramic surface on the resin bonding to the ceramic is still unclear. The effect of four different sandblasting conditions (with 50 and 110 μm alumina at pressures of 0.2 and 0.4 MPa) on the bonding of adhesive resin cement (Panavia F 2.0) to zirconia (Cercon^® ht) was investigated in terms of residual stress. The surface roughness and water contact angle of the zirconia surfaces were measured. The tetragonal-to-monoclinic (t–m) phase transformation and residual stresses (sin²ψ method) were studied by X-ray diffraction. The resin-bonded zirconia specimens were subjected to shear bond strength (SBS) tests before and after thermocycling (10,000 and 30,000 cycles) (n = 10). As the particle size and pressure increased, the roughness gradually and significantly increased (p = 0.023). However, there were no significant differences in roughness-corrected contact angle among all the sandblasted groups (p > 0.05). As the particle size and pressure increased, the m-phase/(t-phase + m-phase) ratios and compressive residual stresses gradually increased. After thermocycling, there were no significant differences in SBS among the sandblasted zirconia groups (p > 0.05). In conclusion, increased surface roughness and residual stress do not directly affect the resin bonding durability.

The present study comprehensively compared the microstructure, flexural strength, and fracture toughness of zirconia ceramics prepared via two different methods, subtractive milling (SM) and stereolithography (SLA). Disc- or rectangular-shaped zirconia specimens (Prettau (SM) and 3DMix Zirconia (SLA)) were prepared following each manufacturer’s instructions and polished. The microstructures of the two different zirconia specimens were studied by scanning electron microscopy, X-ray diffractometry, energy-dispersive X-ray spectroscopy, and electron backscattered diffractometry. The flexural strength and fracture toughness based on the indentation fracture method were measured for the two different zirconia ceramics. A greater number of small pores and smaller grains were found in the SLA specimen than in the SM specimen. The crystal structure and microstructure analysis revealed that both ceramics had a similar phase composition to each other. No significant differences in flexural strength (p = 0.242) or fracture toughness (p = 0.101) were detected between the two ceramics. The mean flexural strength of the SLA-fabricated zirconia as well as the SM zirconia satisfied the class 5 criteria (>800 MPa) in the ISO 6872 standard.

Root canal sealers should have good wetting and adhesion with intraradicular dentin. This study evaluated the wetting and adhesion properties of three bioceramic root canal sealers on dentin using contact angle (CA) measurements and calculations based on the Owens–Wendt–Rabel–Kälble (OWRK) model and compared the properties with those of a resin sealer. Three bioceramic sealers (EndoSequence BC Sealer (BC); Endoseal MTA (EM); and MTA Fillapex (MF)) were tested, together with one epoxy resin-based sealer (AH Plus (AP)). Disc-shaped sealer specimens and human premolar teeth with flat and polished intraradicular dentin surfaces were prepared (n = 12). The CAs of two liquids (water and methylene iodide) were measured on the surfaces using the sessile drop method. The wetting and adhesion properties of the four sealers were calculated using the wetting envelope and isogram diagram, respectively. Group BC showed the best wettability among the four sealer groups. The best adhesion was achieved for group EM, followed by group BC, with a significant difference being present between the two groups (p < 0.05). The OWRK-based calculation indicated that the bioceramic BC and EM sealers showed superior wetting and adhesion properties to the AP sealers.

This study investigated the influence of curing mode (dual- or self-cure) on the surface energy and sorption/solubility of four self-adhesive resin cements (SARCs) and one conventional resin cement. The degree of conversion (DC) and surface energy parameters including degree of hydrophilicity (DH) were determined using Fourier transform infrared spectroscopy and contact angle measurements, respectively (n = 5). Sorption and solubility were assessed by mass gain or loss after storage in distilled water or lactic acid for 60 days (n = 5). A linear regression model was used to correlate between the results (%DC vs. DH and %DC/DH vs. sorption/solubility). For all materials, the dual-curing consistently produced significantly higher %DC values than the self-curing (p < 0.05). Significant negative linear regressions were established between the %DC and DH in both curing modes (p < 0.05). Overall, the SARCs showed higher sorption/solubility values, in particular when immersed in lactic acid, than the conventional resin cement. Linear regression revealed that %DC and DH were negatively and positively correlated with the sorption/solubility values, respectively. Dual-curing of SARCs seems to lower the sorption and/or solubility in comparison with self-curing by increased %DC and occasionally decreased hydrophilicity.

Hwang SK, et al. Restor Dent Endod. 2012 Aug;37(3):165-169. http://dx.doi.org/10.5395/rde.2012.37.3.165