This study focuses on the influence of prolonged ultraviolet (UV) irradiation on the mechanical properties and surface microstructure of glass fiber-reinforced plastics (GFRPs) and basalt fiber-reinforced plastics (BFRPs), which are widely used in construction and transport infrastructure. The relevance of the research lies in the need to improve the reliability of composite materials under extended exposure to harsh climatic conditions. Experimental tests were conducted in a laboratory UV chamber over 2000 h, simulating accelerated weathering. Mechanical properties were evaluated using three-point bending, while surface conditions were assessed via profilometry and microscopy. It was shown that GFRPs exhibit a significant reduction in flexural strength—down to 59–64% of their original value—accompanied by increased surface roughness and microdefect depth. The degradation mechanism of GFRPs is attributed to the photochemical breakdown of the polymer matrix, involving free radical generation, bond scission, and oxidative processes. To verify these mechanisms, FTIR spectroscopy was employed, which enabled the identification of structural changes in the polymer phase and the detection of mass loss associated with matrix decomposition. In contrast, BFRP retained up to 95% of their initial strength, demonstrating high resistance to UV-induced aging. This is attributed to the shielding effect of basalt fibers and their ability to retain moisture in microcavities, which slows the progress of photo-destructive processes. Comparison with results from natural exposure tests under extreme climatic conditions (Yakutsk) confirmed the reliability of the accelerated aging model used in the laboratory.

Regarding a wide variety of PCMs, the materials’ strength properties which decrease no more than 20% after 30 years of operation are of special interest. One of the important regularities of the climatic aging of PCMs is the formation of gradients of mechanical parameters across the thickness of the plates. The occurrence of gradients must be taken into account when modeling the strength of PCMs for long periods of operation. At present, there is no scientific basis for the reliable prediction of the physical-mechanical characteristics of PCMs for a long period of operation in the world of science. Nevertheless, “climatic qualification” has been a universally recognized practice of substantiating the safe operation of PCMs for various branches of mechanical engineering. In this review, the influence of solar radiation, temperature, and moisture according to gradients of mechanical parameters across the thickness of the PCMs are analyzed according to the data of dynamic mechanical analysis, linear dilatometry, profilometry, acoustic emission, and other methods. In addition, the mechanisms of uneven climatic PCM aging are revealed. Finally, the problems of theoretical modeling of uneven climatic aging of composites are identified.

The paper presents the results of studying the effect of borpolymer (BP) on the mechanical properties, structure, and thermodynamic parameters of ultra-high molecular weight polyethylene (UHMWPE). Changes in the mechanical characteristics of polymer composites material (PCM) are confirmed and complemented by structural studies. X-ray crystallography (XRC), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), and infrared spectroscopy (IR) were used to study the melting point, morphology and composition of the filler, which corresponds to the composition and data of the certificate of the synthesized BP. Tensile and compressive mechanical tests were carried out in accordance with generally accepted standards (ASTM). It is shown that BP is an effective modifier for UHMWPE, contributing to a significant increase in the deformation and strength characteristics of the composite: tensile strength of PCM by 56%, elongation at break by 28% and compressive strength at 10% strain by 65% compared to the initial UHMWPE, due to intensive changes in the supramolecular structure of the matrix. Structural studies revealed that BP does not chemically interact with UHMWPE, but due to its high adhesion to the polymer, it acts as a reinforcing filler. SEM was used to establish the formation of a spherulite supramolecular structure of polymer composites.

The purpose of this study was to obtain information on the influence of the size factor on the climatic aging of circular fiber plastics produced by pultrusion. The kinetics of moisture transfer was obtained in humidification and drying modes at 60 °C in samples of epoxy basalt fiber reinforcement bars: after 28 months of exposure in the extremely cold climate of Yakutsk and 30 months of exposure in the moderately warm climate of Gelendzhik. It was shown that the 2D Langmuir model adequately describes the kinetics. The diffusion coefficients in the reinforcement direction for bars with diameters of 6, 8, 10, 16 and 20 mm turned out to be significantly higher than in the radial direction. To clarify the aging mechanism of the bars and the tensile, compressive and bending strength, the coefficient of linear thermal expansion and the glass transition temperature of the epoxy matrix of the bars with a diameter of 6, 8 and 10 mm after 51 months of exposure in Yakutsk and 54 months of exposure in Gelendzhik were measured. It was shown that after climatic exposure, the deformability of the bars decreased with increasing diameter of the bar; the glass transition temperature increased more significantly in the bar with a smaller diameter. In 6 mm diameter bars, the compressive and bending strength limits decreased by 10–25 % due to the plasticizing effect of moisture. With the same depth of moisture penetration into the volume of the samples, its effect on the strength of thin bars was significant, and for thick bars, it was insignificant. An increase in the glass transition temperature by 6 °C, associated with the additional curing of the polymer matrix, occurred in the surface layer of the epoxy basalt fiber reinforcement bars and was revealed in bars with a smaller diameter.