Eco-friendly materials such as poly(lactic acid) (PLA) and cellulose are gaining considerable interest as suitable substitutes for petroleum-based plastics. Therefore, amorphous cellulose (AC) was fabricated as a new reinforcing material for PLA biocomposites by modifying a microcrystalline cellulose (MCC) structure via milling. In this study, the mechanical properties, thermal properties, and degradability of PLA were analysed to compare the effects of both MCC and AC on PLA. The tensile and impact properties improved at an optimum value with AC at 8 wt% and 4 wt% fibre loading, respectively. Notably, a scanning electron micrograph analysis revealed improved AC fibre–matrix adhesion, compared with MCC fibre–matrix adhesion, as well as excellent interaction between AC and PLA. Both MCC and AC improved the hydrolytic degradation of PLA. Moreover, the biocomposites with AC exhibited superior degradation when the incorporation of AC improved the water absorption efficiency of PLA. These findings can expand AC applications and improve sustainability.

Over the last few decades, processing and compatibility have become challenging and interesting investigation areas of polymer matrix nanocomposites. This study investigated the addition of maleic anhydride (MAH) at different ratios with graphene nanoplatelets (GnPs) in poly(lactic acid)/modified natural rubber/polyaniline/GnP (PLA/m-NR/PANI/GnP) nanocomposites via two processing methods: a two-step technique and a one-pot technique. The former technique involved first preparing a master batch of PLA grafted with MAH, followed by a second step involving the melt blending of the nanocomposite (T1) using MAH-g-PLA. On the other hand, the one-pot technique involved the direct mixing of MAH during the melt-blending process (T2). The mechanical, morphological and thermal properties of the prepared nanocomposites were investigated. The findings showed that adding MAH significantly improved the tensile strength and elongation at break by about 25% for PLA/m-NR/PANi/GnP nanocomposites, with an optimal ratio of 1:1 of MAH-g-PLA to GnP loading using the T1 technique. FTIR analysis confirmed the chemical interaction between MAH and PLA for T1 nanocomposites, which exhibited improved phase morphology with smoother surfaces. MAH-compatibilized nanocomposites had enhanced thermal stabilities when compared to the sample without a compatibilizer. The findings show that the compatibilized PLA nanocomposite is potentially suitable for bio-inspired materials.