Binary catalyst nickel oxides (NiO) and manganese oxides (MnO) were prepared individually via hydrothermal route. The catalysts were characterized by scanning electron microscope (SEM), Brunauer-Emmett-Teller (BET) analysis, cyclic voltammetry (CV), and amperometry. Morphology studies revealed physical structure of nanowires nickel oxide and spherical manganese oxide with estimated length of 0.3–2.3 μm and diameter of 0.2–0.8 μm, respectively. Surface areas obtained for nickel oxide and manganese oxide were 68.9 m² g⁻¹and 45.2 m² g⁻¹, respectively. Cyclic voltammetry exhibits electrochemical responses corresponding to the electrode surfaces. The linear responses of the binary catalyst modified gold electrodes with NiO-MnO were observed in the concentration range from 31.8 μM to 0.5 mM with the detection limit of 62.5 μM.

Periodontal disease is an inflammatory disorder that is triggered by bacterial plaque and causes the destruction of the tooth-supporting tissues leading to tooth loss. Several bacteria species, including Porphyromonas gingivalis and Aggregatibacter actinomycetemcomitans, are considered to be associated with severe periodontal conditions. In this study, we demonstrated a quartz crystal microbalance (QCM) immunoassay for quantitative assessment of the periodontal bacteria, A. actinomycetemcomitans. An immunosensor was constructed using a self-assembled monolayer of 11-mercaptoundecanoic acid (11-MUA) on the gold surface of a QCM chip. The 11-MUA layer was evaluated using a cyclic voltammetry technique to determine its mass and packing density. Next, a monoclonal antibody was covalently linked to 11-MUA using 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide/N-hydroxysuccinimide to act as the biorecognition element. The specificity of the monoclonal antibody was confirmed by an enzyme-linked immunosorbent assay. A calibration curve, for the relationship between the frequency shifts and number of bacteria, was used to calculate the number of A. actinomycetemcomitans bacteria in a test sample. Based on a regression equation, the lower detection limit was 800 cells, with a dynamic range up to 2.32 × 10⁶ cells. Thus, the QCM biosensor in this study provides a sensitive and label-free method for quantitative analysis of periodontal bacteria. The method can be used in various biosensing assays for practical application and routine detection of periodontitis pathogens.

Background. External cues are effective in improving gait in people with Parkinson’s disease (PD). However, the most effective cueing method has yet to be determined. Objective. The aim of this study was to compare the immediate effects of using visual, auditory, or somatosensory cues on their own or in combination during walking compared to no cues in people with PD. Methods. This was a single blinded, randomly selected, controlled study. Twenty people with PD with an age range of 46–79 years and Hoehn and Yahr scores of 1–3 were recruited. Participants were studied under 4 cueing conditions; no cue, visual, auditory, or somatosensory cues, which were randomly selected individually or in a combination. Results. A repeated measures ANOVA with pairwise comparisons using Bonferroni correction showed that any single or combination of the cues resulted in an improvement in gait velocity and stride length compared to no cue. Some significant differences were also seen when comparing different combinations of cues, specifically stride length showed significant improvements when additional cues were added to the light cue. The statistically significant difference was set at p < 0.05. Conclusions. Walking using visual, auditory, or somatosensory cues can immediately improve gait mobility in people with PD. Any or a combination of the cues tested could be chosen depending on the ability of the individual to use that cue.

Bio-fuel cell (BFC) using baker's yeast was constructed to examine electricity production. Glucose was used as fuel and electricity was produced by the overall redox reaction in the cell. Neoseptareg membrane was used as proton exchange membrane for separating an anodic compartment and a cathodic compartment. As electron mediator, methylene blue was used for transporting electron from yeast to electrode. Besides, carbon fiber cloth and carbon paper were used as electrodes for comparing the cell performance. Combination of two types of electron acceptor at the cathodic compartment, i.e. potassium ferricyanide and oxygen, were used to optimize efficiency of the system. It was found that electron acceptor affected the voltage generated by the BFC. The best performance was obtained from the system using carbon fiber cloth electrodes and two types of electron acceptors. Open circuit voltage of 450 mV and short circuit current density higher than 165 mA/m² were obtained. Power density of 18 mW/m² was obtained at 750 Omega load