Owing to the inherent nature of the process, typically material produced via electron beam melting (EBM) has a columnar microstructure. As a result of that, the material will have anisotropic mechanical properties. In this work, anisotropic elastic properties of EBM built Alloy 718 samples at room temperature were investigated by using experiments and modelling work. Electron backscatter diffraction data from the sample microstructure was used to predict the Young’s modulus. The results showed that the model developed in the finite element software OOF2 was able to capture the anisotropy in the Young’s modulus. The samples showed transversely isotropic elastic properties having lowest Young’s modulus along build direction. In addition to that, complete transversely isotropic stiffness tensor of the sample was also calculated. This paper is part of a thematic issue on Nuclear Materials.

Electron beam melting (EBM) is a powder bed additive manufacturing process where a powder material is melted selectively in a layer-by-layer approach using an electron beam. EBM has some unique features during the manufacture of components with high-performance superalloys that are commonly used in gas turbines such as Alloy 718. EBM has a high deposition rate due to its high beam energy and speed, comparatively low residual stresses, and limited problems with oxidation. However, due to the layer-by-layer melting approach and high powder bed temperature, the as-built EBM Alloy 718 exhibits a microstructural gradient starting from the top of the sample. In this study, we conducted modeling to obtain a deeper understanding of microstructural development during EBM and the homogenization that occurs during manufacturing with Alloy 718. A multicomponent phase-field modeling approach was combined with transformation kinetic modeling to predict the microstructural gradient and the results were compared with experimental observations. In particular, we investigated the segregation of elements during solidification and the subsequent “in situ” homogenization heat treatment at the elevated powder bed temperature. The predicted elemental composition was then used for thermodynamic modeling to predict the changes in the continuous cooling transformation and time–temperature transformation diagrams for Alloy 718, which helped to explain the observed phase evolution within the microstructure. The results indicate that the proposed approach can be employed as a valuable tool for understanding processes and for process development, including post-heat treatments.

Suspension plasma spraying (SPS) has been shown as a promising process to produce porous columnar strain tolerant coatings for thermal barrier coatings (TBCs) in gas turbine engines. However, the highly porous structure is vulnerable to crack propagation, especially near the topcoat-bondcoat interface where high stresses are generated due to thermal cycling. A topcoat layer with high toughness near the topcoat-bondcoat interface could be beneficial to enhance thermal cyclic lifetime of SPS TBCs. In this work, a bilayer coating system consisting of first a dense layer near the topcoat-bondcoat interface followed by a porous columnar layer was fabricated by SPS using Yttria-stabilised zirconia suspension. The objective of this work was to investigate if the bilayer topcoat architecture could enhance the thermal cyclic lifetime of SPS TBCs through experiments and to understand the effect of the column gaps/vertical cracks and the dense layer on the generated stresses in the TBC during thermal cyclic loading through finite element modeling. The experimental results show that the bilayer TBC had significantly higher lifetime than the single-layer TBC. The modeling results show that the dense layer and vertical cracks are beneficial as they reduce the thermally induced stresses which thus increase the lifetime.

Additive manufacturing of Alloy 718 has become a popular subject of research in recent years. Understanding the process-microstructure-property relationship of additively manufactured Alloy 718 is crucial for maturing the technology to manufacture critical components. Fatigue behaviour is a key mechanical property that is required in applications such as gas turbines. Therefore, in the present work, low cycle fatigue behaviour of Alloy 718 manufactured by laser beam powder bed fusion process has been investigated. The material was tested in as-built condition as well as after two different thermal post-treatments. Three orientations with respect to the building direction were tested to evaluate the anisotropy. Testing was performed at room temperature under controlled amplitudes of strain. It was found that defects, inclusions, strengthening precipitates, and Young’s modulus influence the fatigue behaviour under strain-controlled conditions. The strengthening precipitates affected the deformation mechanism as well as the cycle-dependent hardening/softening behaviour. The defects and the inclusions had a detrimental effect on fatigue life. The presence of Laves phase in LB-PBF Alloy 718 did not have a detrimental effect on fatigue life. Young’s modulus was anisotropic and it contributed to the anisotropy in strain-life relationship. Pseudo-elastic stress vs. fatigue life approach could be used to handle the modulus-induced anisotropy in the strain-life relationship.