We discuss the influence of V-pits and their energy barrier, originating from its facets of ($10\overline{1}1$) planes, on the luminescence efficiency of InGaN LEDs. Experimental analysis using cathodoluminescence (CL) exhibits that thin facets of V-pits of InGaN quantum wells (QWs) appear to be effective in improving the emission intensity, preventing the injected carriers from recombining non-radiatively with threading dislocations (TDs). Our theoretical calculation based on the self-consistent approach with adopting k⋅p method reveals that higher V-pit energy barrier heights in InGaN QWs more efficiently suppress the non-radiative recombination at TDs, thus enhancing the internal quantum efficiency (IQE).

A low-temperature solution-processed high-k gate dielectric layer for use in a high-performance solution-processed semiconducting polymer organic thin-film transistor (OTFT) was demonstrated. Photochemical activation of sol-gel-derived AlOx films under 150 °C permitted the formation of a dense film with low leakage and relatively high dielectric-permittivity characteristics, which are almost comparable to the results yielded by the conventionally used vacuum deposition and high temperature annealing method. Octadecylphosphonic acid (ODPA) self-assembled monolayer (SAM) treatment of the AlO_x was employed in order to realize high-performance (>0.4 cm²/Vs saturation mobility) and low-operation-voltage (<5 V) diketopyrrolopyrrole (DPP)-based OTFTs on an ultra-thin polyimide film (3-μm thick). Thus, low-temperature photochemically-annealed solution-processed AlO_x film with SAM layer is an attractive candidate as a dielectric-layer for use in high-performance organic TFTs operated at low voltages.