In this work, we present a multimodal approach to three-dimensionally quantify and visualize fiber orientation and resin-rich areas in carbon-fiber-reinforced polymers manufactured by vacuum infusion. Three complementary image modalities were acquired by Talbot–Lau grating interferometer (TLGI) X-ray microcomputed tomography (XCT). Compared to absorption contrast (AC), TLGI-XCT provides enhanced contrast between polymer matrix and carbon fibers at lower spatial resolutions in the form of differential phase contrast (DPC) and dark-field contrast (DFC). Consequently, relatively thin layers of resin, effectively indiscernible from image noise in AC data, are distinguishable. In addition to the assessment of fiber orientation, the combination of DPC and DFC facilitates the quantification of resin-rich areas, e.g., in gaps between fiber layers or at binder yarn collimation sites. We found that resin-rich areas between fiber layers are predominantly developed in regions characterized by a pronounced curvature. In contrast, in-layer resin-rich areas are mainly caused by the collimation of fibers by binder yarn. Furthermore, void volume around two adjacent 90°-oriented fiber layers is increased by roughly 20% compared to a random distribution over the whole specimen.

Several methods, including X-ray radiography, have been developed for the investigation of the characteristics of water-saturated quasi-brittle materials. Here, the water content is one of the most important factors influencing their strength and fracture properties, in particular, as regards to porous building materials. However, the research concentrated on the three-dimensional fracture propagation characteristics is still significantly limited due to the problems encountered with the instrumentation requirements and the size effect. In this paper, we study the influence of the water content in a natural quasi-brittle material on its mechanical characteristics and fracture development during in-situ four-point bending by employing high-resolution X-ray differential micro-tomography. The cylindrical samples with a chevron notch were loaded using an in-house designed four-point bending loading device with the vertical orientation of the sample. The in-house designed modular micro-CT scanner was used for the visualisation of the specimen’s behaviour during the loading experiments. Several tomographic scans were performed throughout the force-displacement diagrams of the samples. The reconstructed 3D images were processed using an in-house developed differential tomography and digital volume correlation algorithms. The apparent reduction in the ultimate strength was observed due to the moisture content. The crack growth process in the water-saturated specimens was identified to be different in comparison with the dry specimens.