This study investigates 2 polyethers (PE), 2 polyvinylsiloxanethers (VXSE), and 10 polyvinylsiloxanes (PVS), seven of which had a corresponding light-body consistency and seven of which had a corresponding heavy-body consistency. Each light-body elastomer underwent a flowability test using the shark fin method 20, 50, and 80 s after mixing. The tear strength test DIN 53504 was used after setting the time (T0). Next, 24 h later (T1), hydrophilicity testing was used with static contact angles in water drops during polymerization (20, 50, and 80 s, as well as after 10 min). The heavy-body elastomers underwent shark fin testing with a corresponding light-body material at 50 and 80 s after mixing. The results of light-body testing were combined in a score to describe their performance. The highest differences were detected within flowability in shark fin heights between PE and a PVS (means of 15.89 and 6.85 mm) within the maximum tear strengths at T0 between a PVS and PE (3.72 and 0.75 MPa), as well as within hydrophilicity during setting between VXSE and a PVS (15.09° and 75.5°). The results indicate that VSXE and novel PVS materials can significantly compensate shortcomings in PE towards tear strength and hydrophilicity, but not flowability.

This study determinates the persistence of retention force in Akers-clasps for removable partial dentures made from Co-Cr alloy. Therefore, standardized computer-aided designed (CAD) clasp #1 specimens were made by direct metal laser melting (DMLM, n = 10) and by lost-wax dental casting (DC) of computer-aided manufactured (CAM) replicas (n = 10, DC) from two comparable Co-Cr alloys. The retention force was tested after manufacturing for 9000 cycles of setting and removal from a molar tooth crown analog made from zirconia; simulating in-vitro a duration of six years in service. The first and last 360 cycles (T0 and T1, 3 months each) of all specimens were selected for comparison of retention forces between the materials. A constant decrease of 6% from the initial retention force (T0 = 4.86 N, SD = 0.077; T1 = 4.57 N, SD = 0.037) was detected at the DC specimens, and an increase of 4% in DMLM specimens (T0 = 5.69 N, SD = 0.078; T1 = 5.92 N, SD = 0.077); all differences were statistically significant (p < 0.0001). Even if these deviations are not of clinical relevance, further studies and applications should investigate the fatigue behavior of laser melted Co-Cr-alloys for dental application.