Surgical site infections (SSIs) are one of the most common nosocomial infections, which can result in serious complications after surgical interventions. Foreign materials such as implants or surgical sutures are optimal surfaces for the adherence of bacteria and subsequent colonization and biofilm formation. Due to a significant increase in antibiotic-resistant bacterial strains, naturally occurring agents exhibiting antibacterial properties have great potential in prophylactic therapies. The aim of this study was to develop a coating for surgical sutures consisting of the antibacterial substance totarol, a naturally occurring diterpenoid isolated from Podocarpus totara in combination with poly(lactide-co-glycolide acid) (PLGA) as a biodegradable drug delivery system. Hence, non-absorbable monofilament and multifilament sutures were coated with solutions containing different amounts and ratios of totarol and PLGA, resulting in a smooth, crystalline coating. Using an agar diffusion test (ADT), it became evident that the PLGA/totarol-coated sutures inhibited the growth of Staphylococcus aureus over a period of 15 days. A 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay showed that the coated sutures were not cytotoxic to murine fibroblasts. Overall, the data indicates that our innovative, biodegradable suture coating has the potential to reduce the risk of SSIs and postoperative biofilm-formation on suture material without adverse effects on tissue.

Appropriately adapted comprehensive mechanical properties, degradation behavior and biocompatibility are prerequisites for the application of Zn-based biodegradable implants. In this study, hot-extruded Zn–0.5Cu–xFe (x = 0.1, 0.2 and 0.4 wt%) alloys were fabricated as candidates for biodegradable materials for guided bone regeneration (GBR) membranes. The hot-extrusion process and Cu alloying were expected mostly to enhance the mechanical properties, and the Fe alloying was added mainly for regulating the degradation. The microstructure, mechanical properties and in vitro degradation behavior were systematically investigated. The ZnCuFe alloys were composed of a Zn matrix and FeZn13 phase. With increasing Fe content, a higher FeZn13 phase precipitation with larger particles was observed. Since elongation declined significantly until fracture with increasing Fe content up to 0.4 wt%, the ZnCuFe (0.2 wt%) alloy achieved a good balance between mechanical strength and ductility, with an ultimate tensile strength of 202.3 MPa and elongation at fracture of 41.2%. Moreover, the addition of Fe successfully accelerated the degradation of ZnCuFe alloys. The ZnCuFe (0.2 wt%) alloy showed relatively uniform corrosion in the long-term degradation test. Furthermore, extracts of the ZnCuFe (0.2 wt%) alloy showed no apparent cytotoxic effects against L929 fibroblasts, Saos-2 osteoblasts or TAg periosteal cells. The ZnCuFe (0.2 wt%) alloy exhibited the potential to inhibit bacterial adhesion of Streptococcus gordonii and mixed oral bacteria. Our study provides evidence that the ZnCuFe (0.2 wt%) alloy can represent a promising material for the application as a suitable GBR membrane.

This study investigated the effect of different gaseous plasma surface treatments on the shear bond strength between unfilled polyetheretherketone (PEEK) and veneering composite resin. The study followed ISO 10477 guidelines in preparing, bonding, and testing the samples. Specimens of unfilled PEEK were distributed to one of the following six surface treatment groups: reference, adhesive, argon, nitrogen, oxygen, and air plasmas. After milling, the specimens were wet polished using (P320) polishing discs. Bonding procedures were done according to the manufacturer’s instructions using (Opaquer + Dentine), except in the adhesive group (Visio.link + Opaquer + Dentine). Afterwards, thermal cycling for 5000 cycles between 5 and 55 °C in distilled water was conducted. Finally, the shear bond strengths of all groups were calculated, and mode of fracture was determined. Nitrogen surface treatment had the highest mean shear bond strength of 10.04 (±1.84) MPa, while the reference group showed the lowest value of 5.38 (±2.90) MPa. Regarding mode of fracture, all the specimens showed a 100% adhesive failure mode. Plasma surface treatment can be a reliable alternative method to the traditional protocol of bonding veneering composite resin to unfilled PEEK material.

Encouraging clinical results were reported on a novel cone-in-cone coupling for the fixation of dental implant-supported crowns (Acuris, Dentsply Sirona Implants, Mölndal, Sweden). However, the presence or absence of a microgap and a potential bacterial leakage at the conometric joint has not yet been investigated. A misfit and a resulting gap between the conometric components could potentially serve as a bacterial reservoir that promotes plaque formation, which in turn may lead to inflammation of the peri-implant tissues. Thus, a two-fold study set-up was designed in order to evaluate the bidirectional translocation of bacteria along conometrically seated single crowns. On conometric abutments filled with a culture suspension of anaerobic bacteria, the corresponding titanium nitride-coated (TiN) caps were fixed by friction. Each system was sterilized and immersed in culture medium to provide an optimal environment for microbial growth. Positive and negative controls were prepared. Specimens were stored in an anaerobic workstation, and total and viable bacterial counts were determined. Every 48 h, samples were taken from the reaction tubes to inoculate blood agar plates and to isolate bacterial DNA for quantification using qrt-PCR. In addition, one Acuris test system was subjected to scanning electron microscopy (SEM) to evaluate the precision of fit of the conometric coupling and marginal crown opening. Throughout the observational period of one week, blood agar plates of the specimens showed no viable bacterial growth. qrt-PCR, likewise, yielded a result approaching zero with an amount of about 0.53 × 10−4 µg/mL DNA. While the luting gap/marginal opening between the TiN-cap and the ceramic crown was within the clinically acceptable range, the SEM analysis failed to identify a measurable microgap at the cone-in-cone junction. Within the limits of the in-vitro study it can be concluded that the Acuris conometric interface does not allow for bacterial translocation under non-dynamic loading conditions.