The rational design of high-performance flexible pressure sensors with both high sensitivity and wide linear range attracts great attention because of their potential applications in wearable electronics and human-machine interfaces. Here, polyaniline nanofiber wrapped nonwoven fabric was used as the active material to construct high performance, flexible, all fabric pressure sensors with a bottom interdigitated textile electrode. Due to the unique hierarchical structures, large surface roughness of the polyaniline coated fabric and high conductivity of the interdigitated textile electrodes, the obtained pressure sensor shows superior performance, including ultrahigh sensitivity of 46.48 kPa⁻¹ in a wide linear range (<4.5 kPa), rapid response/relaxation time (7/16 ms) and low detection limit (0.46 Pa). Based on these merits, the practical applications in monitoring human physiological signals and detecting spatial distribution of subtle pressure are demonstrated, showing its potential for health monitoring as wearable electronics.

Copper antimony sulfide (CuSbS₂) has attracted significant interest as an earth-abundant photovoltaic absorber. However, the efficiency of the current CuSbS₂ photovoltaic device is too low to meet the requirement of a large-scale application. In this study, selenylation was introduced to optimize the band structure and improve the device performance. Selenized CuSbS₂ [CuSbS₂(Se)] films were realized using porous CuSbS₂ films prepared by spray deposition with a post-treatment in Se vapor. The as-prepared CuSbS₂(Se) films exhibited a compact structure. X-ray diffraction and elemental analysis confirmed the effective doping of Se into the lattice by substituting a part of S in CuSbS₂. Elemental analysis revealed a gradient distribution for Se from the top surface to the deeper regions, and the substitution rate was very high (>39%). Dark J–V characteristics and AC impedance spectroscopy analysis showed that selenylation significantly reduced the carrier recombination center. As a result, the selenized CuSbS₂ device exhibited a significant efficiency improvement from 0.12% to 0.90%, which is much higher than that of the simply annealed device (0.46%), indicating this technique is a promising approach to improve the performance of CuSbS₂ solar cells.

Broadband AgSbS ₂ (Se) photodetectors are fabricated using spray pyrolysis with a post-selenization process. Indium nitrate is introduced to break the surface blockade to selenidation, largely enhancing the light response range and photocurrent.

Effects of Ca addition on as-cast microstructure, mechanical and corrosion properties of Mg–2Zn–0.3Sr alloy were investigated for biodegradable implant application. First, a comparison between Ca and Sr addition in Mg–2Zn alloy was studied. Mg–2Zn–0.3Sr showed the better corrosion performance, but the worse mechanical property. Then, the results of Ca addition indicated that the dendritic phases dispersed in the Mg matrix. The grains became smaller as Ca content increased. The ultimate tensile strength of Mg–2Zn–0.3Sr–0.3Ca alloy was strengthened to about 170MPa, along with a good ductility of 10%, due to the refinement of grains and homogenous morphology. The ternary alloy had the lowest degradation rate. Mg–2Zn–0.3Sr–0.3Ca still presented a considerable corrosion resistance. 0.5wt% Ca addition brought more and coarser second phases, and worse mechanical and corrosion property. It is suggested that minor addition of Ca (0.1–0.3wt%) in Mg–2Zn–0.3Sr alloy would benefit the practical performance for use in biodegradable implants.

In this study, single-phase Cs_0.33WO₃ nanocrystals were synthesized by a novel mist chemical vapor deposition method. As prepared, Cs_0.33WO₃ nanocrystals exhibited a microsphere-like appearance constructed with angular crystal grains with an average size of about 30–40 nm. Characterization by X-ray photoelectron spectroscopy indicated that Cs_0.33WO₃ nanocrystals consisted of mixed chemical valence states of tungsten ions W⁶⁺ and W⁵⁺, inducing many free electrons, which could scatter and absorb near-infrared (NIR) photons by plasmon resonance. These Cs_0.33WO₃ microspheres consisted of a loose structure that could be crushed to nanoscale particles and was easily applied for producing long-term stable ink after milling. Herein, a Cs_0.33WO₃/polymer composite was successfully fabricated via the ultrasonic spray coating method using mixed Cs_0.33WO₃ ink and polyurethane acrylate solution. The composite coatings exhibited excellent IR shielding properties. Remarkably, only 0.9 mg cm⁻² Cs_0.33WO₃ could shield more than 70% of NIR, while still maintaining the visible light transmittance higher than 75%. Actual measurement results indicate that it has really good heat insulation properties and shows good prospect in heat insulation window applications.