This work studies the possibility of incorporating different proportions of glass powder from the waste glass (rejected material called fine cullet) produced during the glass recycling process into the manufacturing of mortar and concrete. For this purpose, the material is characterized by its chemical composition and pozzolanic activity, and the shape and size of its particles are studied. It is then incorporated as a substitute for cement into the manufacturing of mortar and concrete at 25% and 40% of cement weight, and its effect on setting times, consistency, and mechanical strength is analyzed. Its behavior as a slow pozzolan is verified, and the possibility of incorporating it into concrete is ratified by reducing its cement content and making it a more sustainable material.

The recycling of construction and demolition waste material reduces disposal of material and also the consumption of resources, therefore promoting sustainability in construction. Ultra-high performance concrete (UHPC) is a relatively new material and its feasibility to be recycled needs to be verified. This work investigates the recyclability of UHPC disposed elements, including the production of recycled aggregates and fibres from UHPC. The feasibility of recycled aggregates and fibres at different replacement rates was evaluated through the assessment of rheological and mechanical properties of the newly produced UHPC elements. Concrete mixes with replacement of aggregates at 50% and 100%, displayed compression strength comparable to original UHPC, maintaining the original deflection-hardening response. However, their workability was slightly reduced when increasing the content of the recycled material. Mixes with recycled fibres experienced residual strength losses and behaved as deflection-softening materials in the case of complete replacement.

Three-dimensional printed concrete (3DPC) is a relatively recent technology that may be very important in changing the traditional construction industry. The principal advantages of its use are more rapid construction, lower production costs, and less residues, among others. The choice of raw materials to obtain adequate behavior is more critical than for traditional concrete. In the present paper a mixture of cement, silica fume, superplasticizer, setting accelerator, filler materials, and aggregates was studied to obtain a 3DPC with high resistance at short curing times. When the optimal mixture was found, metallic fibers were introduced to enhance the mechanical properties. The fresh and hard properties of the concrete were analyzed, measuring the setting time, workability, and flexural and compressive strength. The results obtained demonstrated that the incorporation of fibers (2% in volume) enhanced the flexural and compressive strength by around 163 and 142%, respectively, compared with the mixture without fibers, at 9 h of curing. At 28 days of curing, the improvement was 79.2 and 34.7% for flexural and compressive strength, respectively.

This paper presents a study on the development of the cross-curricular learning outcome (CCLO) “Ethical, environmental and professional responsibility” for students of different Bachelor’s Degrees taught at Universitat Politècnica de València (Spain). The work involved in the development of this learning outcome entails great complexity, given the double dimension of responsibility that it involves. At the end of their training at the university, students are expected to show ethical, environmental, and professional responsibility towards themselves and others. Interviews have been conducted with lecturers who work and assess this outcome in their subjects, most/all of them related to science and engineering. The objective was to identify the learning approach used in the different subjects to guarantee the acquisition of this CCLO by the students. A focus group has also been carried out with students to determine the importance they give to this learning outcome, and to know their degree of satisfaction with the training received. The methodology used to obtain the data from lecturers and students and to process the information to get a precise diagnosis is fully described in the paper. Results are satisfactory to some extent: most of the lecturers carry out appropriate activities and most students achieve the expected proficiency level. Finally, recommendations are given to improve the development of this cross-curricular learning outcome.

Supplementary cementitious materials (SCMs) have been used in the construction industry to mainly reduce the greenhouse gas emissions associated with Portland cement. Of SCMs, the petrochemical industry waste known as fluid catalytic cracking catalyst residue (FCC) is recognized for its high reactivity. Nevertheless, the binders produced using SCMs usually present low mechanical strength at early curing ages. This study aims to assess the effect of different accelerating additives (KOH, sodium silicate SIL, commercial additive SKR) on the mechanical strength of mortars containing FCC. The results show that after only 8 curing hours, the compressive strength gain of the FCC mortars containing SKR was over 100% compared to the FCC mortar with no additive (26.0 vs. 12.8 MPa). Comparing the compressive strength of FCC mortar containing SKR to the control mortar, the enhancement is spetacular (6.85 vs. 26.03 MPa). The effectiveness of the tested accelerators at 8–24 curing hours was KOH ≈ SIL < SKR, whereas it was KOH < SIL < SKR for 48 h–28 days. The thermogravimetric data confirmed the good compatibility of FCC and the commercial accelerator.

Los Objetivos de Desarrollo Sostenible en el plan de estudios del Grado en Ingeniería Civil de la Universitat Politècnica de València