To delay acidification and deterioration during natural aging, deacidification and reinforcement of paper manuscripts have been the most important technologies to prolong the life of objects. Herein, a novel approach for the conservation of paper manuscripts is proposed using chitosan nanoparticles as Lewis base that leads to both deacidification and strengthening of paper in one-step. Chitosan nanoparticles were prepared through physical ball grinding method and characterized via scanning electron microscopy (SEM), X-ray diffraction (XRD), laser particle size analyzer (LPSA), Fourier transform infrared spectroscopy (FTIR), and atomic force microscope (AFM). To evaluate the resistance of chitosan nanoparticle coating, the mechanical properties of paper after artificial aging were evaluated using dry heat and hygrothermal accelerated aging methods. The SEM, EDX, and X-ray Photoelectron Spectroscopy (XPS) were used to analyze the interaction mechanism between chitosan and Shuxuan paper. The results show that the coated paper had superior durability with respect to pH, tensile strength, and folding endurance. There was a presence of protonated amines in the form of ammonium salts due to ionic bindings with free H⁺ in the acidified paper, and the remaining –NH₂ could be used as a base reserve. Finally, the resulting coated papers displayed good antibacterial properties.

Paper acidification causes paper relics to undergo embrittlement and decay, to form dregs, and even to break upon a single touch; therefore, reinforcement and deacidification treatments are essential steps for paper conservation and to retard the deterioration and prolong the life of objects. Polymeric adhesives play an essential role in reinforcement and deacidification treatments, although it is not well studied. In this work, the effect of polymeric adhesives on the conservation process and their protective effects on acidified paper relics were studied. Firstly, three polymeric adhesives, including wheat starch paste, polyvinyl butyral (PVB), and polyvinyl alcohol (PVA), were selected as research objects. Subsequently, their effects on four popular conservation methods were further discussed, including traditional mounting, hot-melt with silk net, alcohol-soluble cotton mesh, and water-soluble cotton mesh. Additionally, as an example, the reversibility and long-term durability of water-soluble adhesive PVA-217 were assessed. Using a computer measured and controlled folding endurance tester, pendulum tensile strength tester, tear tester, burst tester, FT-IR, video optical contact angle tester, and other instruments, the conservation application of water-soluble adhesives in paper relics was evaluated. This study provides a scientific basis and experimental data for the application of polymeric adhesives in the conservation of paper relics.

Deacidification plays an important role in the conservation of paper-based cultural heritage objects. Herein, a novel approach for the conservation of scale paper-based cultural heritage objects is proposed using a mixture of argon and ethylene oxide (EO-Ar) for the first time. The optimum process conditions for deacidification of ethylene oxide and argon mixture system are determined by orthogonal testing. To evaluate the stabilization effect of paper treated with EO-Ar, the degradation of the mechanical properties (tensile strength, folding endurance and tearing strength tests) of paper after artificial aging was evaluated. The results show that the treated paper had better durability with respect to tensile strength, folding endurance and tearing strength. Additionally, thermal stability, crystallinity and fiber wall thickness increased after EO-Ar treated, which was determined by scanning electron microscope (SEM), diffraction of X-rays (XRD), and thermo gravimetric (TG) analysis. Some compounds, such as polyethylene glycol, organic acids, esters, were detected by GC-MS after treatment with EO-Ar. Two hundred and forty books including acidic, weak acidic and alkaline books were successfully deacidified, resulting in pH values of paper ranges suitable for paper preservation. Finally, a possible mechanism of deacidification of EO-Ar was proposed.

Some painted pottery figurines were excavated from the tomb of Qibi Ming of the Tang Dynasty. A series of analytical techniques were employed to understand the craftsmanship of these painted pottery figurines. The pigment, cross-section, adhesive, and firing temperature were analyzed using microscopy (OM), energy X-ray fluorescence spectrometry (EDX), micro-Raman spectroscopy, pyrolysis–gas chromatography–mass spectrometry (Py-GC/MS), and a dilatometer (DIL). The results demonstrated that the surface of the pigment layers had degraded to different degrees. The pigment particles were litharge, gypsum, malachite, cinnabar, hematite, minium, white lead, and carbon black. The cross-sectional images show that the painted layer of figurines 10-0966 and 10-0678 included a pigment layer and a preparation layer. The preparation layer of both pigments was lead white. Animal glue was used as an adhesive. The firing temperature of the pottery figurines was likely 1080 °C. This study can provide more accurate information with regard to the composition of the raw materials utilized in the making of these artifacts and support the selection of appropriate substances for the purposes of conservation and restoration of the painted pottery figurines.