Based on the establishment of the original and improved models of the turbine blade, a thermal-fluid-solid coupling method and a finite element method were employed to analyze the internal and external flow, temperature, and thermal stress of the turbine blade. The uneven temperature field, the thermal stress distribution characteristics of the composite cooling turbine blade under the service conditions, and the effect of the thickness of the thermal barrier coating (TBC) on the temperature and thermal stress distributions were obtained. The results show that the method proposed in this paper can better predict the ablation and thermal stress damage of turbine blades. The thermal stress of the blade is closely related to the temperature gradient and local geometric structure of the blade. The inlet area of the pressure side-platform of the blade, the large curvature region of the pressure tip of the blade, and the rounding between the blade body and the platform on the back of the blade are easily damaged by thermal stress. Cooling structure optimization and thicker TBC thickness can effectively reduce the high temperature and temperature gradient on the surface and inside of the turbine blade, thereby reducing the local high thermal stress.

In this paper, high temperature erosion tests are performed on four typical anti-erosion coatings for high-parameter steam turbine blades using pneumatic accelerated erosion method to simulate the actual erosion environment in power units. With the employment of scanning electron microscope, energy-dispersive X-ray spectroscopy, glancing-angle X-ray diffraction, and Vickers indentation testing techniques, detailed microscopic analysis of samples is conducted to reveal the underlying causes affecting the anti-erosion performance of coatings. Results show that, under the solid particle erosion at high temperature, boride coatings with more compact structure and higher hardness have stronger anti-erosion ability, whose erosion rate is only 30–50% that of HVOF Cr₃C₂ coatings under the same erosion condition. Boride coatings composed of duplex phase (FeB and Fe₂B) have lower anti-erosion damage capability than that of boride coatings composed of single Fe₂B phase. Under high-speed large incidence angle impingement, the surface layer of FeB cracks easily and rapidly propagates to the subsurface layer Fe₂B phase under the sustained impingement from particles, resulting in the flaking off and failure of coatings. Single Fe₂B phase boride coatings have smaller hardness gradient in the depth direction and higher fracture toughness than boride coatings composed of duplex phase, so that exhibit more stable excellent erosion resistance under different erosion parameters. Therefore, single Fe₂B phase boride coatings should be used as the preferred wear resistant coating for turbine blades solid particle erosion problem.

Reducing solid particle erosion (SPE) of blades is one of the most urgent problems for supercritical steam turbine power generation technology. Based on the erosion rate models and the particle rebound models of blade materials obtained through the accelerated erosion test under high temperature, erosion characteristics of the first reheat stage blades in a supercritical steam turbine was simulated and analyzed by three-dimensional numerical simulation method in this paper. The influence of operating conditions, particle size distribution in the inlet of nozzle, and axial clearance between vanes and rotating blades on the erosion distribution of cascade were explored quantitatively. Results show that the erosion damage of the first-reheat stage stator is mainly caused by suction surface impingement from oxide particles. In designed loading condition, small and medium size of particles mainly eroded the trailing edge (TE) of nozzle pressure surface, while large particles mainly impinge the leading edge (LE) of rotating blades and the TE of vane suction surface, and erosion increase along the blade height. When the turbine is running under part-load condition, particle impingement angle on stator pressure surface is basically unchanged, while impingement velocity slightly reduced. However, the amount of particles that impinge the stator TE suction side after their first-time impingement on rotor LE increase rapidly, leading to the more severe erosion damage of stator suction surface. The particle size distribution in the inlet of nozzle has a significant effect on the erosion simulation of first reheat stage blades, and the size distribution sampled in one unit may not be used to other units. When axial clearance changes, the erosion weight loss of vane pressure surface near TE is basically held constant, while the erosion weight loss in vane suction surface near TE decreases with the increase of axial clearance. For the supercritical 600 MW unit simulated in this article, the antiSPE performance and the unit efficiency can be balanced well when the axial clearance increases to 13 mm. The results in this paper will provide a technology basis for reducing oxide particle erosion in the first reheat stage blades of supercritical steam turbine.

In this study, the high temperature erosion mechanisms and damage characteristics of a boronized coating have been systematically studied by employing an improved high-temperature accelerated erosion test bench and impact contact theory analyses. Within the scope of the experimental parameters, the erosion rate of the boronized coating under the same erosion conditions was observed to be only one half to one-twelfth of the erosion rate of the substrate. Furthermore, the boronized coating was noted to be less sensitive to the speed of the erosion particles than the plastic substrate, thus, indicating superior and more stable erosion resistance than the base material. The boronized coating exhibited typical brittle fracture characteristics under impact by the high-speed particles. When the particle impact normal stress exceeded the critical stress for crack propagation owing to the coating defects, the surface and subsurface layers of the coating initially formed horizontal and vertical micro-cracks, followed by their gradual expansion and intersection. After destabilization, the brittle coating material was peeled layer-by-layer from the surface of the test piece. At the same incident speed, as the particle size was increased from 65 μm to 226 μm and 336 μm, the size (width) of the erosion cracks on the coating surface increased from 1 μm to 30 μm and 100 μm respectively. Correspondingly, the erosion damage thickness of the coating was enhanced from 15 μm to 50 μm and 100 μm. In the case of the quartz sand particle size exceeding 300 μm, the dual-phase boronized coating did not provide effective protection to the substrate. Furthermore, based on the elastoplastic fracture theory, a prediction model for the erosion weight loss of the boronized coatings within the effective thickness range has been proposed in this study.

Reducing solid particle erosion of blades is one of the most urgent problems for high-parameter steam turbine power generation technology. Based on the erosion rate model and particle rebound model of blade materials obtained through accelerated erosion test under high temperature, erosion characteristics of flaky particles in control stage of a typical supercritical steam turbine were systemically studied using three-dimensional numerical simulation method. The erosion mechanism of hard coatings on nozzle suction surface is first revealed, and erosion resistance of boride coating with large oxide particles is validated through high-temperature erosion test. Results show that serious erosion damage of boride coating on the latter half of nozzle suction surface is caused by the combined rebounded impingement of large particles between 1000 µm and 2000 µm after their initial impingement on the nozzle pressure surface and the leading edge of rotating blade. The average particle impingement velocity can reach up to 150–180 m/s, and the impingement angle is in the range of 18°–28°. High-temperature erosion test results show that boride coating will soon broken and fall off under the continuing impact of millimeter-sized particles, which confirms that hard coatings are difficult to resist the high-intensity impingement from these large particles. Therefore, separating particles before entering the nozzle chamber with the employment of an inertial separator should be the optimal choice for improving the erosion resistance of turbine. The results of this study enrich the types of blade erosion damage and provide a new idea for reducing erosion damage of control stage blades.