We give a comprehensive overview of how the morphology control is an effective and versatile way to control the physicochemical properties of metal oxides that can be transferred to metal–organic frameworks and porous carbon materials.

A series of TiO₂-ZnO binary oxide systems with various molar ratios of TiO₂ and ZnO were prepared using a sol-gel method. The influence of the molar ratio and temperature of calcination on the particle sizes, morphology, crystalline structure, surface composition, porous structure parameters, and thermal stability of the final hybrids was investigated. Additionally, to confirm the presence of characteristic surface groups of the material, Fourier transform infrared spectroscopy was applied. It was found that the crystalline structure, porous structure parameters, and thermal stability were determined by the molar ratio of TiO₂ to ZnO and the calcination process for the most part. A key element of the study was an evaluation of the photocatalytic activity of the TiO₂-ZnO hybrids with respect to the decomposition of C.I. Basic Blue 9, C.I. Basic Red 1, and C.I. Basic Violet 10 dyes. It was found that the TiO₂-ZnO material obtained with a molar ratio of TiO₂:ZnO = 9:1 and calcined at 600 °C demonstrates high photocatalytic activity in the degradation of the three organic dyes when compared with pristine TiO₂. Moreover, an attempt was made to describe equilibrium aspects by applying the Langmuir-Hinsherlwood equation.

Zinc oxide, as a widely used material in optics, electronics, and medicine, requires a complete overview of different conditions for facile and easily reproducible syntheses. Two types of optimization of ZnO hydrothermal preparation from zinc acetate and sodium hydroxide solution are presented, which allowed for obtaining miscellaneous morphologies of materials. The first was a temperature-controlled synthesis from 100 to 200 °C, using citric acid as a capping agent. The formation of hexagonal rods at the lowest temperature was evidenced, which agglomerated to flower-like structures at 110 and 120 °C. It was followed by transformation to flake-like roses at 160 °C, up to disordered structures composed of nanosized plates (>180 °C). The transformations were generated through a temperature change, which had an impact on the diffusion effect of hydroxide and citrate complexes. The second optimization was the hydrothermal synthesis free of organic additives and it included only a pH variation from 7.5 to 13.5. It was found that by utilizing a slow-dropping process and varying amounts of NaOH solutions, it is possible to obtain well-formed hexagonal pellets at pH 8.0–8.5. Strongly basic conditions of pH 11.0 and 13.5 impeded superstructure formations, giving small elongated particles of ZnO. All samples were characterized by high phase purity and crystallinity, with a specific surface area of 18–37 m²/g, whereas particle size distribution indicated a predominance of small particles (<1 μm).