Novel, functional materials based on chitin of marine origin and lignin were prepared. The synthesized materials were subjected to physicochemical, dispersive-morphological and electrokinetic analysis. The results confirm the effectiveness of the proposed method of synthesis of functional chitin/lignin materials. Mechanism of chitin modification by lignin is based on formation of hydrogen bonds between chitin and lignin. Additionally, the chitin/lignin materials were studied from the perspective of waste water treatment. The synthetic method presented in this work shows an attractive and facile route for producing low-cost chitin/lignin biosorbents with high efficiency of nickel and cadmium adsorption (88.0% and 98.4%, respectively). The discovery of this facile method of synthesis of functional chitin/lignin materials will also have a significant impact on the problematic issue of the utilization of chitinous waste from the seafood industry, as well as lignin by-products from the pulp and paper industry.

A series of TiO₂-ZnO binary oxide systems with various molar ratios of TiO₂ and ZnO were prepared using a sol-gel method. The influence of the molar ratio and temperature of calcination on the particle sizes, morphology, crystalline structure, surface composition, porous structure parameters, and thermal stability of the final hybrids was investigated. Additionally, to confirm the presence of characteristic surface groups of the material, Fourier transform infrared spectroscopy was applied. It was found that the crystalline structure, porous structure parameters, and thermal stability were determined by the molar ratio of TiO₂ to ZnO and the calcination process for the most part. A key element of the study was an evaluation of the photocatalytic activity of the TiO₂-ZnO hybrids with respect to the decomposition of C.I. Basic Blue 9, C.I. Basic Red 1, and C.I. Basic Violet 10 dyes. It was found that the TiO₂-ZnO material obtained with a molar ratio of TiO₂:ZnO = 9:1 and calcined at 600 °C demonstrates high photocatalytic activity in the degradation of the three organic dyes when compared with pristine TiO₂. Moreover, an attempt was made to describe equilibrium aspects by applying the Langmuir-Hinsherlwood equation.

In recent years, groundwater contamination caused by dyes has become an important problem. They enter into wastewater as a result of the textile, automotive, or cosmetics industries. For this reason, new methods are being sought, which would aid at the removal of dye impurities with high efficiency and also would be relatively cheap. In the presented study synthesized TiO₂-ZrO₂ (with TiO₂:ZrO₂ molar ratio of 8:2) and TiO₂-ZrO₂-SiO₂ (with TiO₂:ZrO₂:SiO₂ molar ratio of 8:1:1) oxide materials were used as supports for enzyme immobilization. Effective synthesis of the carriers was confirmed by results of scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), low-temperature nitrogen sorption and Fourier transform infrared spectroscopy (FTIR). The materials achieve high immobilization efficiency of the laccases from Trametes versicolor (83% and 96% for TiO₂-ZrO₂-laccase and TiO₂-ZrO₂-SiO₂-laccase, respectively). The effect of selected dye concentrations, pH, temperature, and reusability were also tested. The obtained results showed that after removal of textile dyes, such as Alizarin Red S (ARS), Remazol Brilliant Blue R (RBBR), and Reactive Black 5 (RB5), under optimal process conditions, which were pH 5 and 25 °C, from dye solution of 5 mg/L degradation efficiency reached 100%, 91%, and 77%, respectively, suggesting synergistic mechanism of degradation by simultaneous sorption and catalytic action. Finally, reduction of chemical oxygen demand (COD) of the solution after treatment indicated lower mixture toxicity and effective dye degradation.

In this study, titania nanoparticles were obtained using the microwave-assisted technique. Moreover, different surfactants (PEG (M_n = 400), Pluronic P123 and Triton X−100) were used during the synthesis in order to determine their impact on the crystallinity and morphology of the final products. Subsequently, techniques such as XRD, SEM and TEM (performed in high contrast and high-resolution mode), diffuse reflectance spectroscopy (DRS), low temperature N₂ sorption (BET model), FTIR and TGA were carried out. Based on the crystallinity analysis of the obtained materials, it was established that the addition of surfactants results in greater (PEG and Triton X−100) or smaller (Pluronic P123) average crystallite size. The main purpose of this study was to use the synthesized nanomaterials in the photodegradation process (in the UV light range) of the model organic pollutants – phenol (20 mg/L) and etodolac (15 mg/L). Furthermore, it was also pointed out that the dye-sensitized solar cells can be a second application for the synthesized titania nanomaterials. The photo-oxidation and photovoltaic tests have shown that the titanium dioxide obtained using the surfactant-assisted microwave method is characterized not only by better photodegradation efficiency of phenol and etodolac, but also by higher photocurrent density compared to the reference titania samples—the pristine TiO₂ and commercial P25.

Titania has properties that enable it to be used in a variety of applications, including self-cleaning surfaces, air and water purification systems, hydrogen evolution, and photoelectrochemical conversion. In order to improve the properties of titanium dioxide, modifications are made to obtain oxide/hybrid systems that are intended to have the properties of both components. In particular, zinc oxide, zirconia and molybdenum disulfide have been proposed as the second component of binary systems due to their antibacterial, electrochemical and photocatalytic properties. This paper presents a review of the current state of knowledge on the synthesis and practical utility of TiO₂-ZnO and TiO₂-ZrO₂ oxide systems and TiO₂-MoS₂ hybrid materials. The first part focuses on the hydrothermal method; then a review is made of the literature on the synthesis of the aforementioned materials using the sol-gel method. In the last section, the literature on the electrospinning method of synthesis is reviewed. The most significant physico-chemical, structural and dispersive-morphological properties of binary hybrid systems based on TiO₂ are described. A key aim of this review is to indicate the properties of TiO₂-ZnO, TiO₂-ZrO₂ and TiO₂-MoS₂ hybrid systems that have the greatest importance for practical applications. The variety of utilities of titania-based hybrid materials is emphasized.