This research focused on the synthesis of a functional alginate-based material via chemical modification processes with two steps: oxidation and reductive amination. In previous alginate functionalization with a target molecule such as cysteine, the starting material was purified and characterized by UV-Vis, ¹H-NMR and HSQC. Additionally, the application of FT-IR techniques during each step of alginate functionalization was very useful, since new bands and spiked signals around the pyranose ring (1200–1000 cm⁻¹) and anomeric region (1000–750 cm⁻¹) region were identified by a second derivative. Additionally, the presence of C₁-H₁ of β-D-mannuronic acid residue as well as C₁-H₁ of α-L-guluronic acid residue was observed in the FT-IR spectra, including a band at 858 cm⁻¹ with characteristics of the N-H moiety from cysteine. The possibility of attaching cysteine molecules to an alginate backbone by oxidation and post-reductive amination processes was confirmed through ¹³C-NMR in solid state; a new peak at 99.2 ppm was observed, owing to a hemiacetal group formed in oxidation alginate. Further, the peak at 31.2 ppm demonstrates the presence of carbon -CH₂-SH in functionalized alginate—clear evidence that cysteine was successfully attached to the alginate backbone, with 185 μmol of thiol groups per gram polymer estimated in alginate-based material by UV-Visible. Finally, it was observed that guluronic acid residue of alginate are preferentially more affected than mannuronic acid residue in the functionalization.

In the present study, Fe₃O₄/poly(2-hydroxyethyl methacrylate-co-itaconic acid) magnetic hydrogels (MHGs) were prepared by in situ synthesis of Fe₃O₄ magnetic particles in hydrogels (HGs). The resulting magnetic hydrogels were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), a vibrating sample magnetometer (VSM), scanning electron microscopy (SEM), and N₂ adsorption–desorption. The effect of Fe₃O₄ on the swelling behavior and adsorption of methylene blue (MB) dye of the prepared hydrogel was studied. Parameters such as the dose, pH, contact time, and MB initial concentration were investigated. The results show that 75% (HG) and 91% (MHG) of MB (200 mg/L) were removed at doses of 2 mg/mL and 1 mg/mL, respectively, under a pH of 6.8 and a contact time of 10 min. The adsorption behavior followed the Langmuir isotherm model, indicating that the adsorption process takes place in monolayers and on homogeneous surfaces. The Langmuir capacities for MB adsorption using the HGs and MHGs were 78 and 174 mg/g, respectively. The adsorption kinetics followed a pseudo-second-order kinetic model. In addition, thermodynamic studies carried out show that the adsorption process is spontaneous and endothermic. Adsorption–desorption studies indicate that the magnetic hydrogel can remove MB for four cycles with removal efficiencies above 90%. Therefore, a MHG is suitable as an alternative material for MB adsorption.

An increase in the production of cationic dyes is expected over the next decade, which will have an impact on health and the environment. This work reports an adsorbent hydrogel composed of poly(acrylic acid) [poly(AA)] and Fe₃O₄ particles, prepared by radical polymerization and in situ co-precipitation of Fe³⁺ and Fe²⁺. This Fe₃O₄/poly(AA) composite hydrogel was used to evaluate its potential for removing the cationic dyes methylene blue (MB) and crystal violet (CV) from aqueous solutions. Instrumental characterization of the hydrogel was performed by FTIR, XRD, TGA, VSM, and physicochemical analysis (swelling and response to changes in pH). The results show that the incorporation of Fe₃O₄ particles improves the adsorption capacity of MB and CV dyes to a maximum adsorption of 571 and 321 mg/g, respectively, under the best conditions (pH 6.8, dose 1 g/L, time 24 h). The adsorption data best fit the pseudo-first order (PFO) kinetic model and the Freundlich isothermal model, indicating mass transfer via internal and/or external diffusion and active sites with different adsorption potentials. Moreover, the thermodynamic analysis confirmed that the adsorption process was spontaneous and exothermic, with physisorption as the dominant mechanism. In addition, the Fe₃O₄/poly(AA) hydrogel is capable of removing 95% of the dyes after ten consecutive adsorption–desorption cycles, demonstrating the potential of hydrogels loaded with Fe₃O₄ particles for the treatment of wastewater contaminated with dyes.