Electromechanical response of materials is a key property for various applications ranging from actuators to sophisticated nanoelectromechanical systems. Here electromechanical properties of the single-layer graphene transferred onto SiO₂ calibration grating substrates is studied via piezoresponse force microscopy and confocal Raman spectroscopy. The correlation of mechanical strains in graphene layer with the substrate morphology is established via Raman mapping. Apparent vertical piezoresponse from the single-layer graphene supported by underlying SiO₂ structure is observed by piezoresponse force microscopy. The calculated vertical piezocoefficient is about 1.4 nm V⁻¹, that is, much higher than that of the conventional piezoelectric materials such as lead zirconate titanate and comparable to that of relaxor single crystals. The observed piezoresponse and achieved strain in graphene are associated with the chemical interaction of graphene’s carbon atoms with the oxygen from underlying SiO₂. The results provide a basis for future applications of graphene layers for sensing, actuating and energy harvesting.

The use of engineered cardiac tissue for high-throughput drug screening/toxicology assessment remains largely unexplored. Here we propose a scaffold that mimics aspects of cardiac extracellular matrix while preserving the contractility of cardiomyocytes. The scaffold is based on a poly(caprolactone) (PCL) nanofilm with magnetic properties (MNF, standing for magnetic nanofilm) coated with a layer of piezoelectric (PIEZO) microfibers of poly(vinylidene fluoride-trifluoroethylene) (MNF+PIEZO). The nanofilm creates a flexible support for cell contraction and the aligned PIEZO microfibers deposited on top of the nanofilm creates conditions for cell alignment and electrical stimulation of the seeded cells. Our results indicate that MNF+PIEZO scaffold promotes rat and human cardiac cell attachment and alignment, maintains the ratio of cell populations overtime, promotes cell-cell communication and metabolic maturation, and preserves cardiomyocyte (CM) contractility for at least 12 days. The engineered cardiac construct showed high toxicity against doxorubicin, a cardiotoxic molecule, and responded to compounds that modulate CM contraction such as epinephrine, propranolol and heptanol.

Li-ion battery performance and life cycle strongly depend on a passivation layer called solid-electrolyte interphase (SEI). Its structure and composition are studied in great details, while its formation process remains elusive due to difficulty of in situ measurements of battery electrodes. Here we provide a facile methodology for in situ atomic force microscopy (AFM) measurements of SEI formation on cross-sectioned composite battery electrodes allowing for direct observations of SEI formation on various types of carbonaceous negative electrode materials for Li-ion batteries. Using this approach, we observed SEI nucleation and growth on highly oriented pyrolytic graphite (HOPG), MesoCarbon MicroBeads (MCMB) graphite, and non-graphitizable amorphous carbon (hard carbon). Besides the details of the formation mechanism, the electrical and mechanical properties of the SEI layers were assessed. The comparative observations revealed that the electrode potentials for SEI formation differ depending on the nature of the electrode material, whereas the adhesion of SEI to the electrode surface clearly correlates with the surface roughness of the electrode. Finally, the same approach applied to a positive LiNi_1/3Mn_1/3Co_1/3O₂ electrode did not reveal any signature of cathodic SEI thus demonstrating fundamental differences in the stabilization mechanisms of the negative and positive electrodes in Li-ion batteries.