This investigation studies the effects of hot water and hot air curing on the strength development, transport properties, and freeze-thaw resistance of mortars incorporating low-heat blast furnace slag cement and nanosilica (NS). Mortar samples were prepared and stored in ambient conditions for 24 h. After demolding, mortar samples were subjected to two different hot curing methods: Hot water and hot air curing (40 °C and 60 °C) for 24 h. For comparison purposes, mortar reference mixes were prepared and cured in water and air at ambient conditions. Strength development (from 1 to 180 days), capillary water porosity, water sorptivity, and freeze-thaw resistance were tested after 180 days of curing. The experimental results showed that both curing regimes accelerate the strength development of mortars, especially in the first seven days of hydration. The highest early strengths were reported for mortars subjected to a temperature of 60 °C, followed by those cured at 40 °C. The hot water curing regime was found to be more suitable, as a result of more stable strength development. Similar findings were observed in regard to durability-related properties. It is worth noting that thermal curing can more efficiently increase strength in the presence of nanosilica, suggesting that NS is more effective in enhancing strength under thermal curing.

The utilization of waste crushed clay brick (CB) in concrete reduces its harmful impacts on the environment as it can be found in many places around the world. This research studies the possibility of using clay brick powder (CBP) as a filler material to produce lightweight concrete as it has been exposed to high temperatures during manufacturing of the bricks, which increases its pozzolanic reactivity. The effect of using an air-entraining agent (AEA) for additional pore formation on concrete performance was evaluated. Eight mixtures were prepared and examined to achieve the research objectives. Concrete flowability, dry density, compressive strength, ultrasonic pulse velocity, thermal conductivity, sorptivity, and porosity were measured. Additionally, scanning electron microscopy, X-ray diffraction, thermo-gravimetric analysis, and mercury intrusion porosimetry were used to analyze the microstructure characteristics of the concrete. The results indicate that the use of CBP as filler material enhances the mechanical and durability characteristics of the concrete. In contrast, adding an AEA has negative effects on concrete’s mechanical and durability properties, but on the other hand, its use enhances the thermal properties of the concrete.

Hybrid cement (HC) can be defined as alkali activated-blended-Portland cement (PC). It is prepared by the addition of an alkaline solution to high-volume aluminosilicate-blended-PC. Although this cement exhibits higher mechanical performance compared to conventional blended one (aluminosilicate–PC blend), it represents lower commercial viability because of the corrosive nature of alkaline solution. Therefore, this study focuses on the preparing one-part HC using dry activator–based BFS (DAS). DAS was prepared by mixing sodium hydroxide (NaOH) with BFS at low water to BFS ratio, followed by drying and grinding to yield DAS-powder. Different contents of DAS (equivalent to 70 wt.% BFS and 1, 2, and 3 wt.% NaOH) were blended with 30 wt.% PC. A mixture containing 70 wt.% BFS and 30 wt.% PC was used as a reference sample. The mortar was adjusted at a sand–powder (BFS-PC and/or DAS-PC) weight ratio of 3:1. The microstructural analysis proved that DAS-powder is mainly composed of sodium calcium aluminosilicate–activated species and unreacted BFS. These species can interact again with water to form calcium aluminum silicate hydrate (C-A-S-H) and NaOH, suggesting that the DAS acts as a NaOH-carrier. One-part HC mortars having 1, 2, and 3 wt.% NaOH recorded 7th day compressive strength values of 82%, 44%, and 27%, respectively, higher than that of the control sample. At 180 days of curing, a significant reduction in compressive strength was observed within the HC mortar having 3 wt.% NaOH. This could be attributed to the increase of Ca (within C-S-H) replacement by Na, forming a Na-rich phase with lower binding capacity. The main hydration products within HC are C-S-H, C-A-S-H, and chabazite as part of the zeolite family.

This study reports a potential approach for the valorization of glass waste (GW) that is mainly composed of amorphous silica to prepare lightweight foamed glass (FG). The preparation of FG was achieved by mixing sodium hydroxide with GW powder followed by sintering at a temperature of 800 °C. As-synthesized FG was characterized and applied as an effective adsorbent for the removal of hazardous organic water contaminants, in particular, methylene blue (MB) dye. FG exhibited porosity of 91%, bulk density of 0.65 g/cm³, compressive strength of 4 MPa, and thermal conductivity of 0.27 W/m·K. Theoretical treatment indicated that a monolayer model with one energy site was the best in fitting the removal of MB molecules. The number of MB molecules per active site (n) ranged from 2.20 to 1.70, suggesting vertical orientation and a multi-molecular adsorption mechanism. The density of FG receptor sites (D_M) increased with the temperature, and this parameter played a vital role in the adsorption process. The adsorption capacity (Q_sat) increased from 255.11 to 305.58 mg/g, which signifies endothermic interactions. MB adsorption on FG was controlled by physical forces such as electrostatic interactions (i.e., the adsorption energies were <20 kJ/mol). The results of this study prove the feasibility of glass waste as an effective and low-cost adsorbent for water remediation.