The aim of this work is to characterize the rolling and rolling-sliding contact fatigue failure mechanisms on the 32CrMoV13 nitrided steel. During rolling contact fatigue tests (RCF), two general features were observed: specimens presenting short lives and rough and sharpened spalling damage and specimens presenting long lives and only microspalling marks. It was possible to determine a contact fatigue limit of 3 GPa. During rolling-sliding contact fatigue tests (RSCF), a clearly different behaviour between the two specimens in contact has been observed: the driver shows circumferential and inclined cracks and only inclined cracks appear in the follower. This behaviour can be understood if the effect of the residual stress state in near-surface layers is considered. Before RCF tests, the residual stresses are compressive in all near-surface layers. After RCF tests, strong residual stress relaxation and even reversing behaviour was observed in the axial direction, which facilitates the surface crack initiation in the circumferential direction at rolling track borders.

Rolling contact fatigue twin-disc tests were performed on rail/wheel steels from Spanish high velocity trains (AVE). Residual stress profiles were determined using X-ray diffraction before and after cyclic loading. The evolution of residual stress profiles, due to cyclic loading, was analysed in order to study how they affect the rolling contact fatigue behaviour of these materials. This study is included in a major project where other related phenomena and materials’ properties have been studied.

A hybrid experimental-numerical methodology is applied to evaluate the unwanted stresses induced by hole-drilling in two 5000 and 7000 series aluminium alloys. The influence of the cutting speed of ultra-high speed drills powered by turbine systems by compressed air, which are commonly used in the hole-drilling equipments for residual stress measurements, is analyzed. The comparison of the effect of different drilling conditions on the drilled material using a quantitative approach is now possible. The applied methodology can play an important role on the improvement and optimization of the hole-drilling technique for residual stress measurements in particular and the drilling process in general.

Twin disc tribological tests were performed in wheel and rail materials, with specimens taken from a Spanish AVE train wheel and a UIC60 rail, in a program intended to characterize their contact fatigue behavior. The X-ray diffraction technique was used to characterize the residual stress distribution at the initial and damaged stages, as well as in intermediate stages, since existing residual stresses in the surface layers of the railways steels and its evolution during contact loading can have a major influence on crack initiation and propagation.