In this study, the phase transformation behaviour of the carburised layer and the matrix of 23CrNi3Mo steel was comparatively investigated by constructing continuous cooling transformation (CCT) diagram, determining the volume fraction of retained austenite (RA) and plotting dilatometric curves. The results indicated that Austenite formation start temperature (Ac1) and Austenite formation finish temperature (Ac3) of the carburised layer decreased compared to the matrix, and the critical cooling rate (0.05 °C/s) of martensite transformation is significantly lower than that (0.8 °C/s) of the matrix. The main products of phase transformation in both the carburised layer and the matrix were martensite and bainite microstructures. Moreover, an increase in carbon content resulted in the formation of lamellar martensite in the carburised layer, whereas the martensite in the matrix was still lath. Furthermore, the volume fraction of RA in the carburised layer was higher than that in the matrix. Moreover, the bainite transformation kinetics of the 23CrNi3Mo steel matrix during the continuous cooling process indicated that the mian mechanism of bainite transformation of the 23CrNi3Mo steel matrix is two-dimensional growth and one-dimensional growth.

In this study, the decomposition of a martensite/austenite (M/A) microconstituent in bainitic steels was analyzed using differential scanning calorimetry (DSC) data in conjunction with Kissinger’s and Johnson–Mehl–Avrami–Kolmogorov (JMAK)’s formulas. In bainitic steel subjected to austempering heat treatment, the presence of an M/A microstructure adversely affects the mechanical properties. According to the kinetic equations derived, it is observed that after tempering the sample at 600 °C for 4000 s, the generation of each phase reaches its maximum. The SEM images taken before and after tempering reveal extensive decomposition of the M/A constituent in the microstructure. The proportion of the M/A microstructure decreased significantly from about 10% before tempering to less than 1% after. Additionally, the content of residual austenite also reduced nearly to zero. These observations are consistent with the predictions of the kinetic equations.

The effects of carbide precipitation on mechanical performance of Hybrid Steel 60, known as a novel bearing steel, have not been investigated. In this study, the austenite transformation temperatures of Hybrid Steel 60 during heating were revealed by the thermal expansion curve. The temperature and effective activation energy of the second phase precipitation were determined by the differential scanning calorimetry (DSC) curve. Different solid solution structures after austenitization were detected using various cooling rates. The solubility temperature was determined based on hardness and residual austenite content. The carbides precipitated at the peak temperature were qualitatively identified using XRD. It was discovered that the temperature points Ac1 and Ac3 of the steel were 786 °C and 864 °C, respectively. In addition, the effect of solid solution temperature on quenching hardness is minimal, while the cooling rate has a greater impact on hardness, reaching a peak at 5 °C s⁻¹. The primary carbide phase in Hybrid Steel 60 is the M₇C₃ and VC. When the temperature ranges from 500 °C to 550 °C, M₂₃C₆ begins to precipitate. As a result, after tempering at 525 °C, the hardness peak value reached 566 HV.