A multi-strand composite welding wire was applied to join high nitrogen austenitic stainless steel, and microstructures and mechanical properties were investigated. The electrical signals demonstrate that the welding process using a multi-strand composite welding wire is highly stable. The welded joints are composed of columnar austenite and dendritic ferrite and welded joints obtained under high heat input and cooling rate have a noticeable coarse-grained heat-affected zone and larger columnar austenite in weld seam. Compared with welded joints obtained under the high heat input and cooling rate, welded joints have the higher fractions of deformed grains, high angle grain boundaries, Schmid factor, and lower dislocation density under the low heat input and cooling rate, which indicate a lower tensile strength and higher yield strength. The rotated Goss (G_RD) ({110}〈1 $\overline{1}$ 0〉) orientation of a thin plate and the cube (C) ({001}〈100〉) orientation of a thick plate are obvious after welding, but the S ({123}〈63 $\overline{4}$ 〉) orientation at 65° sections of Euler’s space is weak. The δ-ferrite was studied based on the primary ferrite solidification mode. It was observed that low heat input and a high cooling rate results in an increase of δ-ferrite, and a high dislocation density was obtained in grain boundaries of δ-ferrite. M₂₃C₆ precipitates due to a low cooling rate and heat input in the weld seam and deteriorates the elongation of welded joints. The engineering Stress–strain curves also show the low elongation and tensile strength of welded joints under low heat input and cooling rate, which is mainly caused by the high fraction of δ-ferrite and the precipitation of M₂₃C₆.

The main purpose of this work was to investigate the microstructure and mechanical properties of spray-formed 2195-T6 Al-Li alloy welding joints produced by tungsten inert gas (TIG) with Al-Cu and Al-Si-Cu filler wires, so that they can be better used in space vehicle tanks. The porosity analysis indicates that the porosity area of the weld seam with the Al-Si-Cu filler wire is approximately 7.989 times larger than that of the Al-Cu filler wire. Furthermore, the microstructure and microhardness results indicate that the Al/Cu eutectic near the fusion line distributes more at the grain boundaries, while more dispersed Al₂Cu phase is found inside the grain, which improves the strength of the joint when using Al-Cu filler wire. However, when using the Al-Si-Cu filler wire, more Si, Cu, and Ti elements are segregated at the grain boundaries, forming a brittle-hard network Al/Cu/Ti eutectic, which reduces the performance of the joint. Additionally, the tensile strength and elongation of the weld joint are about 68.6% and 89.9% of the base metal (BM) when using the Al-Cu filler wire, and can approach the level of friction stir welding (FSW). However, the tensile strength and elongation are only about 56.8% and 39.9%, respectively, of the BM in the weld joint when using the Al-Si-Cu filler wire. Lastly, the fractures both occur on the fusion line and the fracture morphology of the weld joint shows that it is a mixed fracture mode dominated by plastic fracture when using Al-Cu filler wire, while it is mainly a quasi-cleavage fracture mode when using Al-Si-Cu filler wire. Therefore, the joint strength when using Al-Si-Cu filler wire with high strength matching is not as good as that of Al-Cu filler wire with low strength matching.

High-efficiency and high-quality welding has always been the focus of welding research. This article proposes a novel double-pulse, triple-wire MIG welding process for the welding of 6082-T6 aluminum alloy. The process characteristics of welding arc and droplet transfer were studied, and the performances of weld formation, morphology, hardness, and tensile strength were tested for the 1 Hz, 3 Hz, and 5 Hz double-pulse welding and normal-pulse welding. It was found that in the welding process, the pulsed arc steadily alternated among three welding wires without arc interruption, and the arc length changed periodically with the double-pulse frequency. The droplets transferred with a stable one-pulse-one-drop mode. Besides, a proper double-pulse frequency, e.g., 3 Hz in this case, was conducive to forming good welds with regular fish-scale patterns and no pores. The tensile strength of the joint could reach 64% of the base material’s tensile strength, and its fracture belonged to plastic fracture, which occurred in the HAZ. This new welding method will have great potential in aluminum alloy welding.

Multi-wire welding has received much attention in the machinery industry due to its high efficiency. The aim of this study was to investigate a novel pulse gas metal arc welding (GMAW) that has circular triple-wire electrodes. The effect of the pulse phage angle on arc stability was particularly studied. Research showed that for typical phase angles the arc stability from low to high is 180°, 0°, and 120°, and the arcs are very stable at 120°. The triple-wire welding was used to weld a 9 mm thick Q960E steel, which is typically used for the arm of construction machinery. When the welding heat input was controlled at 1.26–1.56 kJ/mm, the weld zone was dominated by acicular ferrite, and the coarse-grained zone of the heat-affected zone was a mixed structure of lath martensite and lath bainite. The tensile strength of the welded joint reached 85% of the base metal and the impact toughness was above 62 J, which can meet the requirements of construction machinery. This indicates that the triple-wire welding has great potential to achieve efficient and high-quality welding for the construction machinery.