Aluminium–copper composite materials were successfully fabricated using spark plasma sintering with Al and Cu powders as the raw materials. Al–Cu composite powders were fabricated through a ball milling process, and the effect of the Cu content was investigated. Composite materials composed of Al–20Cu, Al–50Cu, and Al–80Cu (vol.%) were sintered by a spark plasma sintering process, which was carried out at 520 °C and 50 MPa for 5 min. The phase analysis of the composite materials by X-ray diffraction (XRD) and energy-dispersive spectroscopy (EDS) indicated that intermetallic compounds (IC) such as CuAl₂ and Cu₉Al₄ were formed through reactions between Cu and Al during the spark plasma sintering process. The mechanical properties of the composites were analysed using a Vickers hardness tester. The Al–50Cu composite had a hardness of approximately 151 HV, which is higher than that of the other composites. The thermal conductivity of the composite materials was measured by laser flash analysis, and the highest value was obtained for the Al–80Cu composite material. This suggests that the Cu content affects physical properties of the Al–Cu composite material as well as the amount of intermetallic compounds formed in the composite material.

Al–Cu composites have attracted significant interest recently owing to their lightweight nature and remarkable thermal properties. Understanding the interdiffusion mechanism at the numerous Al/Cu interfaces is crucial to obtain Al–Cu composites with high thermal conductivities. The present study systematically investigates the interdiffusion mechanism at Al/Cu interfaces in relation to the process temperature. Al-50vol.%Cu composite powder, where Cu particles were encapsulated in a matrix of irregular Al particles, was prepared and then sintered at various temperatures from 340 to 500 °C. Intermetallic compounds (ICs) such as CuAl₂ and Cu₉Al₄ were formed at the Al/Cu interfaces during sintering. Microstructural analysis showed that the thickness of the interdiffusion layer, which comprised the CuAl₂ and Cu₉Al₄ ICs, drastically increased above 400 °C. The Vickers hardness of the Al-50vol.%Cu composite sintered at 380 °C was 79 HV, which was 1.5 times that of the value estimated by the rule of mixtures. A high thermal conductivity of 150 W∙m⁻¹∙K⁻¹ was simultaneously obtained. This result suggests that the Al-50vol.%Cu composite material with large number of Al/Cu interfaces, as well as good mechanical strength and heat conductance, can be prepared by solid-state sintering at a low temperature.

Al–Cu matrix composites with excellent mechanical and thermal properties are among the most promising materials for realising high performance in thermal management systems. However, intermetallic compounds (ICs) formed at the Al/Cu interfaces prevent direct contact between the metals and severely deteriorate the thermal conductivity of the composite. In this study, we systemically investigated the formation behaviour of Al–Cu ICs as a function of compaction pressure at a low temperature of 380 °C. The phases of the Al–Cu ICs formed during sintering were detected via X-ray diffraction, and the layer thickness and average area fraction of each IC at different compaction pressures were analysed via micro-scale observations of the cross-sections of the Al–Cu composites. The ICs were partially formed along the Al/Cu interfaces at high pressures, and the formation region was related to the direction of applied pressure. The Vickers hardness of the Al–Cu composites with ICs was nearly double those calculated using the rule of mixtures. On the other hand, the thermal conductivity of the composites increased with compaction pressure and reached 201 W·m⁻¹·K⁻¹. This study suggests the possibility of employing Al–Cu matrix composites with controlled IC formation in thermal management applications.

Aluminum (Al)-stainless steel 316L (SUS316L) composites were successfully fabricated by the spark plasma sintering process (SPS) using pure Al and SUS316L powders as raw materials. The Al-SUS316L composite powder comprising Al with 50 vol.% of SUS316L was prepared by a ball milling process. Subsequently, it was sintered at 630 °C at a pressure of 200 MPa and held for 5 min in a semisolid state. The X-ray diffraction (XRD) patterns show that intermetallic compounds such as Al₁₃Fe₄ and AlFe₃ were created in the Al-SUS316L composite because the Al and SUS316L particles reacted together during the SPS process. The presence of these intermetallic compounds was also confirmed by using XRD, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and EDS mapping. The mechanical hardness of the Al-SUS316L composites was analyzed by a Vickers hardness tester. Surprisingly, the Al-SU316L composite exhibited a Vickers hardness of about 620 HV. It can be concluded that the Al-SUS316L composites fabricated by the SPS process are lightweight and high-hardness materials that could be applied in the engineering industry such as in automobiles, aerospace, and shipbuilding.

The low oxygen powder metallurgy technique makes it possible to prepare full-dense ultrafine-grained (UFG) Al compacts with an average grain size of 160 nm by local surface bonding at a substantially lower temperature of 423 K from an Al nanopowder prepared by a low oxygen induction thermal plasma process. By atomic level analysis using transmission electron microscopy, it was found that there was almost no oxide layer at the Al/Al interfaces (grain boundaries) in UFG Al compact. The electrical conductivity of the UFG Al compact reached 3.5 × 10⁷ S/m, which is the same level as that of the cast Al bulk. The Vickers hardness of the UFG Al compact of 1078 MPa, which is 8 times that of the cast Al bulk, could be explained by the Hall–Petch law. In addition, fracture behavior was analyzed by conducting a small punch test. The as-sintered UFG Al compact initially fractured before reaching its ultimate strength due to its large number of grain boundaries with a high misorientation angle. Ultimate strength and elongation were enhanced to 175 MPa and 24%, respectively, by reduction of grain boundaries after annealing, indicating that high compatibility of strength and elongation can be realized by appropriate microstructure control.