In the paper, a novel technique for highly dispersed pyrochlore Y₂Ti₂O₇ is proposed. The experimental results proved that the application of microwave irradiation at a certain stage of calcination allowed synthesizing of Y₂Ti₂O₇ in much shorter time, which ensured substantial energy savings. An increase up to 98 wt.% in the content of the preferred phase with a pyrochlore-type structure Y₂Ti₂O₇ was obtained after 25 h of yttrium and titanium oxides calcination at a relatively low temperature of 1150 °C, while the microwave-supported process took only 9 h and provided 99 wt.% of pyrochlore. The proposed technology is suitable for industrial applications, enabling the fabrication of large industrial amounts of pyrochlore without solvent chemistry and high-energy mills. It reduced the cost of both equipment and energy and made the process more environmentally friendly. The particle size and morphology did not change significantly; therefore, the microwave-assisted method can fully replace the traditional one.

Journal of Nano- and Electronic Physics. Scientific journal. ISSN: 2077-6772. Journal abbreviation: J. Nano- Electron. Phys. No page charges. All articles are freely available on-line. Issued 4 times per year. Publisher: Sumy State University. (Sumy, Ukraine)

Journal of Nano- and Electronic Physics. Scientific journal. ISSN: 2077-6772. Journal abbreviation: J. Nano- Electron. Phys. No page charges. All articles are freely available on-line. Issued 4 times per year. Publisher: Sumy State University. (Sumy, Ukraine)

Complex studies of the formation of the superhard state in the TiZrHfNbTaYN vacuum-arc high-entropy coating were carried out. Based on the approach of the structural surface engineering, the...

Multilayer (TiSi)N/CrN coatings were fabricated through vacuum-arc deposition by applying the arc currents of (100 ÷ 110) A on TiSi cathode and (80 ÷ 90) A on Cr cathode, negative bias potential connected to the substrate holder of –(100 ÷ 200) V and reactive gas pressure of (0.03 ÷ 0.6) Pa. Applying a negative bias voltage on substrates enhanced the ion bombardment effect, which affected the chemical compositions, phase state, mechanical and tribological properties of (TiSi)N/CrN coatings. Obtained results indicated that (TiSi)N/CrN coatings with Si content ranging from 0.53 to 1.02 at. % exhibited a high hardness level of (22.1 ÷ 31.1) GPa accompanied with a high Young’s modulus of (209 ÷ 305) GPa, H/E* level of (0.080 ÷ 0.100), H3/E*2 level of (0.15 ÷ 0.33) GPa, and the friction coefficient of 0.35. Values of critical loads at dynamic indentation, changes in friction coefficient and level of acoustic emission signal evidence the high adhesive strength of (TiSi)N/CrN coatings, which allows recommending them to increase cutting tool performance.