Wood is a truly sustainable and aesthetically pleasant material used in indoor and outdoor applications. Every material, including wood, is expected to have long-term durability and to retain its original appearance over time. One of the major disadvantages of wood is the deterioration of its surface when exposed outdoors, known as weathering. Although weathering is primarily a surface phenomenon, it is an important issue for wood products as it affects their appearance, service life, and wood-coating performance. To encourage the use of wood as a material for joinery and other building components, the results of research into increasing the weathering resistance of wood are extremely significant. The development of weathering protection methods is of great importance to reduce the maintenance requirements for wood exposed outdoors and can have a major environmental impact. There are various methods of protecting wood surfaces against weathering. This paper provides a literature survey on the recent research results in protecting wood from weathering. The topics covered include surface treatments of wood with photostabilizers; protection with coatings; the deposition of thin film onto wood surfaces; treatments of wood with inorganic metal compounds and bio-based water repellents; the chemical modification of wood; the modification of wood and wood surfaces with thermosetting resins, furfuryl alcohol, and DMDHEU; and the thermal modification of wood.

Heat treatment is a method of wood modification with increasing market acceptance in Europe. The major patented European commercial heat treatment processes have trade names ThermoWood, Platowood, Retiwood, Le Bois Perdure, and Oil-Heat-Treated Wood (OHT). To what extent modification of wood affects the resistance of wood to weathering is also an important aspect for wood applications, especially where appearance is important. Unfortunately, heat-treated wood has poor resistance to weathering, and surface treatment with coatings is required for both protection and aesthetic reasons. As a substrate for coating, heat-treated wood has altered characteristics such as lower hygroscopicity and liquid water uptake and changed acidity, wettability, surface free energy, and anatomical microstructure. Various wood species, heat treatment method, treatment intensity, and treatment conditions exhibited a different extent of changes in wood properties. These altered properties could affect coating performance on heat-treated wood. The reported changes in acidity and in surface energy due to heat treatments are inconsistent with one another depending on wood species and temperature of the treatments. This paper gives an overview of the research results with regards to properties of heat-treated wood that can affect coating performance and weathering of uncoated and coated heat-treated wood.

Oriented strand board (OSB) is a commonly used structural wood-based panel for walls and roof siding, but recently the industry has become interested in OSB as a substrate for indoor and outdoor furniture. Particleboard is mainly used in furniture productions and has become popular as a construction material due to its numerous usage possibilities and inexpensive cost. Moisture is one of the most important factors affecting wood-based panel performance and the post-treatment conditions affected their affinity to water. When OSB and particleboard are used as substrates for coatings, their surface characteristics play an important role in determining the quality of the final product. Furthermore, roughness can significantly affect the interfacial phenomena such as adsorption, wetting, and adhesion which may have an impact on the coating performance. In this research particleboard and OSB panels were sanded, re-pressed and IR heated and the influence of surface treatments on hardness, roughness, wetting, water, and water vapour absorption was studied. Results showed that sanding improved the wetting of particleboard and OSB with water. Moreover, studied surface treatments increased water absorption and water penetration depth of OSB panels, and re-pressing had a positive effect on reducing the water vapour absorption of particleboard and OSB panels.

In this research, the influence of titanium dioxide (TiO₂) nanoparticles and their modifications on the weathering resistance of untreated and heat-treated wood was studied. The wood samples were coated with polyacrylate waterborne emulsion coatings that contain nano-TiO₂ in the amount of 0.75 wt.%. Two types of modifiers were used to modify the nano-TiO₂ surface: 2,2′-azobis(2-methylpropionamide) dihydrochloride (AIBA) and 3-aminopropyltrimethoxy silane (AMPTS). Coated and uncoated wood samples were exposed to accelerated weathering by application of sunlight, water and moisture for 360 h. During the research, the dry film thickness, color, gloss and hardness of the surface of the samples were measured. The obtained results showed that the effect of the addition and surface modification of nano-TiO₂ on the color and gloss stability was different on untreated and heat-treated ash wood, and that accelerated weathering causes an increase in surface hardness and a decrease in thickness of the dry coating.

The present study investigates the relationship between the roughness of beech wood and oak wood surfaces treated with oil and polyurethane coating and the slip resistance in dry, water-wet and oily conditions. Pendulum tests were...