Wood is a truly sustainable and aesthetically pleasant material used in indoor and outdoor applications. Every material, including wood, is expected to have long-term durability and to retain its original appearance over time. One of the major disadvantages of wood is the deterioration of its surface when exposed outdoors, known as weathering. Although weathering is primarily a surface phenomenon, it is an important issue for wood products as it affects their appearance, service life, and wood-coating performance. To encourage the use of wood as a material for joinery and other building components, the results of research into increasing the weathering resistance of wood are extremely significant. The development of weathering protection methods is of great importance to reduce the maintenance requirements for wood exposed outdoors and can have a major environmental impact. There are various methods of protecting wood surfaces against weathering. This paper provides a literature survey on the recent research results in protecting wood from weathering. The topics covered include surface treatments of wood with photostabilizers; protection with coatings; the deposition of thin film onto wood surfaces; treatments of wood with inorganic metal compounds and bio-based water repellents; the chemical modification of wood; the modification of wood and wood surfaces with thermosetting resins, furfuryl alcohol, and DMDHEU; and the thermal modification of wood.

Heat treatment is a method of wood modification with increasing market acceptance in Europe. The major patented European commercial heat treatment processes have trade names ThermoWood, Platowood, Retiwood, Le Bois Perdure, and Oil-Heat-Treated Wood (OHT). To what extent modification of wood affects the resistance of wood to weathering is also an important aspect for wood applications, especially where appearance is important. Unfortunately, heat-treated wood has poor resistance to weathering, and surface treatment with coatings is required for both protection and aesthetic reasons. As a substrate for coating, heat-treated wood has altered characteristics such as lower hygroscopicity and liquid water uptake and changed acidity, wettability, surface free energy, and anatomical microstructure. Various wood species, heat treatment method, treatment intensity, and treatment conditions exhibited a different extent of changes in wood properties. These altered properties could affect coating performance on heat-treated wood. The reported changes in acidity and in surface energy due to heat treatments are inconsistent with one another depending on wood species and temperature of the treatments. This paper gives an overview of the research results with regards to properties of heat-treated wood that can affect coating performance and weathering of uncoated and coated heat-treated wood.

This paper deals with the effect of UV light through window glass on the changes in colour of surfaces of uncoated and clear-coated thermally modified wood, and on chemical changes of surfaces of uncoated thermally modified and unmodified wood. Discoloration of the uncoated wood samples and those treated with three commercial transparent coatings (two-component polyurethane varnish, water-borne varnish, and nano-impregnation) was measured spectrophotometrically using CIELAB parameters (L*, a*, b* and DE*). FTIR spectroscopy was used to study chemical changes caused by UV irradiation. Colour change (DE*) was recorded in all tested wood samples after exposure to UV light, and the smallest discoloration was recorded in wood samples coated with two-component polyurethane varnish. FTIR spectroscopy results show that thermal treatment and exposure to UV light modified the chemical structure of wood surface and that the thermally modified samples exposed to UV light showed similar changes as unmodified samples exposed to UV light, but less pronounced.

This paper studies the influence of ammonia gas on wood color changes in response to an increasing demand for dark colored wood specimens. The darker wood color in ammonia fuming is accomplished through chemical reactions between ammonia gas and wood compounds. We exposed oak, maple, spruce, and larch wood samples to ammonia gas for 16 days. During fuming, the color changes were studied using CIE L*a*b* parameters. After fuming, the changes in extractives content, tannin, and nitrogen content were analyzed. The chemical changes of wood and residues of wood extractives after fuming were analyzed by FTIR spectroscopy. Oak wood reacted intensively with ammonia gas in a very short time, and the darkening was prominent for all the investigated wood species. It was established that tannin had no major influence on color changes of maple and larch wood in the ammonia-fuming process. The FTIR spectra of fumed wood indicated involvement of carbonyl groups, and the FTIR spectra of wood extractives indicated involvement of carbonyl, aromatic, and alcohol groups in reaction with ammonia gas.

Oriented strand board (OSB) is a commonly used structural wood-based panel for walls and roof siding, but recently the industry has become interested in OSB as a substrate for indoor and outdoor furniture. Particleboard is mainly used in furniture productions and has become popular as a construction material due to its numerous usage possibilities and inexpensive cost. Moisture is one of the most important factors affecting wood-based panel performance and the post-treatment conditions affected their affinity to water. When OSB and particleboard are used as substrates for coatings, their surface characteristics play an important role in determining the quality of the final product. Furthermore, roughness can significantly affect the interfacial phenomena such as adsorption, wetting, and adhesion which may have an impact on the coating performance. In this research particleboard and OSB panels were sanded, re-pressed and IR heated and the influence of surface treatments on hardness, roughness, wetting, water, and water vapour absorption was studied. Results showed that sanding improved the wetting of particleboard and OSB with water. Moreover, studied surface treatments increased water absorption and water penetration depth of OSB panels, and re-pressing had a positive effect on reducing the water vapour absorption of particleboard and OSB panels.

Knowing the properties of wood-based building materials is essential for their proper use. Moisture transfer properties of building materials are crucial to proper building design and the prevention of moisture-related problems. In selecting materials for the building, it is important to know their water vapour transmission properties. In this research the water vapour transmission properties of uncoated and coated particleboard, oriented strand board (OSB) and birch plywood were studied using wet cup method and a moisture gradient in the samples was additionally measured. The water vapour transmission rate of free films of three commercial transparent coatings was also studied. Results showed that particleboard had the highest water vapour permeability and that the coatings reduced the water vapour permeability of all tested wood-based panels. Moreover, sanding increased the water vapour permeability of uncoated particleboard and OSB. The moisture gradient in all tested wood-based panels was linear. The highest water vapour transmission rate was recorded for acrylic water-borne coating, followed by polyurethane water-borne coating and the lowest for polyurethane solvent-based coating.