To reveal the effect of chlorine substituents in the ring of aromatic amine on the synthesis process of benzoxazine monomer and on its polymerization ability, as well as to develop a fire-resistant material, a previously unreported benzoxazine monomer based on 3,3′-dichloro-4,4′-diaminodiphenylmethane was obtained in toluene and mixture toluene/isopropanol. The resulting benzoxazine monomers were thermally cured for 2 h at 180 °C, 4 h at 200 °C, 2 h at 220 °C. A comparison between the rheological, thermal and fire-resistant properties of the benzoxazines based on 3,3′-dichloro-4,4′-diaminodiphenylmethane and, for reference, 4,4′-diaminodimethylmethane was made. The effect of the reaction medium on the structure of the oligomeric fraction and the overall yield of the main product were studied and the toluene/ethanol mixture was found to provide the best conditions; however, in contrast to most known diamine-based benzoxazines, synthesis in the pure toluene is also possible. The synthesized monomers can be used as thermo- and fire-resistant binders for polymer composite materials, as well as hardeners for epoxy resins. Chlorine-containing polybenzoxazines require more severe conditions for polymerization but have better fire resistance.

The kinetics of the sorption of water vapor on powders of crab-shell chitin and chitosan are studied via the methods of static sorption, thermography, and X-ray structural analysis. Sorption isotherms are obtained in the range of humidity from 10 to 95%. S-Shaped water-sorption isotherms observed for all chitin and chitosan samples are approximated via superpositioning of Langmuir and Flory-Huggins isotherms. The water-polysaccharide interaction parameters and the maximum sorption capacities of water located in chitin and chitosan are determined. The cluster integral is calculated, and the moisture values corresponding to water-cluster formation are determined. The water-diffusion coefficients are determined, and the effective activation energies of water diffusion are estimated: 70 kJ/mol in chitosan and 60 kJ/mol in chitin. The data on the concentration dependences of the coefficients of diffusion of water in the powdered chitin and chitosan are summarized.

Structural and morphological features of graft polystyrene (PS) and polyethylene (PE) copolymers produced by post-radiation chemical polymerization have been investigated by methods of X-ray microanalysis, electron microscopy, DSC and wetting angles measurement. The studied samples differed in the degree of graft, iron(II) sulphate content, sizes of PE films and distribution of graft polymer over the polyolefin cross section. It is shown that in all cases sample surfaces are enriched with PS. As the content of graft PS increases, its concentration increases both in the volume and on the surface of the samples. The distinctive feature of the post-radiation graft polymerization is the stepped curves of graft polymer distribution along the matrix cross section. A probable reason for such evolution of the distribution profiles is related to both the distribution of peroxide groups throughout the sample thickness and to the change in the monomer and iron(II) salt diffusion coefficients in the graft polyolefin layer. According to the results of electron microscope investigations and copolymer wettability during graft polymerization, a heterogeneous system is formed both in the sample volume and in the surface layer. It is shown that the melting point, glass transition temperature and degree of crystallinity of the copolymer decreases with the increasing proportion of graft PS. It is suggested that during graft polymerization a process of PE crystallite decomposition (melting) and enrichment of the amorphous phase of graft polymer by fragments of PE macromolecules occurs spontaneously. The driving force of this process is the osmotic pressure exerted by the phase network of crystallites on the growing phase of the graft PS.

The compositions based on bimodal high-density polyethylene (HDPE, copolymer of ethylene with hexene-1) and in mixture with monomodal tercopolymer of ethylene with butene-1/hexene-1 (LLDPE, low-density polyethylene) have been studied. Phase equilibrium, thermodynamic parameters of interdiffusion in a wide range of temperatures and ratios of co-components were identified by refractometry, differential scanning calorimetry, optical laser interferometry, X-ray phase analysis. The phase state diagrams of the HDPE—LLDPE systems were constructed. It has been established that they belong to the class of state diagrams of “solid crystal solutions with unrestricted mixing of components”. The paired parameters of the components interaction and their temperature dependences were calculated. Thermodynamic compatibility of α-olefins in the region of melts and crystallization of one of the components has been shown. The kinetics of formation of interphase boundaries during crystallization of α-olefins has been analyzed. The morphology of crystallized gradient diffusion zones has been analyzed by optical polarization microscopy. The sizes of spherulites in different areas of concentration profiles and values of interdiffusion coefficients were determined.

The effect of molecular mass, thermal prehistory, physical state, and three-dimensional chemical crosslinked structure of a polymer on dissolution and diffusion in the PVP-water system has been...

The state of sorbed water molecules in the matrix of polyvinyl alcohol is investigated via the methods of static sorption, DSC, TGA, IR Fourier spectroscopy, ¹H NMR spectroscopy, and quantum-chemical simulation. It is shown that the sorption of water by polyvinyl alcohol characterized by an S-shaped isotherm is described by the double-sorption model. It is established that the low diffusion coefficients and extremely low rates of desorption processes observed in the range of low activities are determined by a shift of the equilibrium toward the formation of hydrogen-bonded complexes of water molecules with hydroxy groups of the polymer. A mechanism for the behavior of residual water in hydrophilic polymers is suggested. It implies that differences between polymers are determined only by the quantity of residual water immobilized in “traps” and the energy of hydrogen-bond formation.