Bulk quantities of defect-free silicon (Si) nanowires with nearly uniform diameters ranging from 40 to 50 angstroms were grown to a length of several micrometers with a supercritical fluid solution-phase approach. Alkanethiol-coated gold nanocrystals (25 angstroms in diameter) were used as uniform seeds to direct one-dimensional Si crystallization in a solvent heated and pressurized above its critical point. The orientation of the Si nanowires produced with this method could be controlled with reaction pressure. Visible photoluminescence due to quantum confinement effects was observed, as were discrete optical transitions in the ultraviolet-visible absorbance spectra.

Au nanoparticles with diameters ranging between 15 and 170 nm have been synthesised in aqueous solution using a seed-mediated growth method, employing hydroxylamine hydrochloride as a reducing agent. Thiolated polyethylene glycol (mPEG-SH) polymers, with molecular weights ranging from 2100 to 51 000 g mol⁻¹, were used as efficient particle stabilising ligands. Dynamic light scattering and zeta potential measurements confirmed that the overall mean diameter and zeta potential of the capped nanoparticles increased in a non-linear way with increasing molecular weight of the mPEG-SH ligand. Electron microscopy and thermal gravimetric analysis of the polymer-capped nanoparticles, with a mean gold core diameter of 15 nm, revealed that the grafting density of the mPEG-SH ligands decreased from 3.93 to 0.31 PEG nm⁻² as the molecular weight of the ligands increased from 2100 to 51 400 g mol⁻¹ respectively, due to increased steric hindrance and polymer conformational entropy with increase in the PEG chain length. Additionally, the number of bound mPEG-SH ligands, with a molecular weight of 10 800 g mol⁻¹, was found to increase in a non-linear way from 278 (σ = 42) to approximately 12 960 PEG (σ = 1227) when the mean Au core diameter increased from 15 to 115 nm respectively. However, the grafting density of mPEG_10 000-SH ligands was higher on 15 nm Au nanoparticles and decreased slightly from 1.57 to 0.8 PEG nm⁻² when the diameter increased; this effect can be attributed to the fact that smaller particles offer higher surface curvature, therefore allowing increased polymer loading per nm². Au nanoparticles were also shown to interact with CT-26 cells without causing noticeable toxicity.

Development of multifunctional nanomaterials, one of the most interesting and advanced research areas in the field of nanotechnology, is anticipated to revolutionize cancer diagnosis and treatment. Gold nanoparticles (AuNPs) are now being widely utilized in bioimaging and phototherapy due to their tunable and highly sensitive optical and electronic properties (the surface plasmon resonance). As a new concept, termed “theranostics,” multifunctional AuNPs may contain diagnostic and therapeutic functions that can be integrated into one system, thereby simultaneously facilitating diagnosis and therapy and monitoring therapeutic responses. In this review, the important properties of AuNPs relevant to diagnostic and phototherapeutic applications such as structure, shape, optics, and surface chemistry are described. Barriers for translational development of theranostic AuNPs and recent advances in the application of AuNPs for cancer diagnosis, photothermal, and photodynamic therapy are discussed.