In dentistry, maxillofacial surgery, traumatology, and orthopedics, there is a need to use osteoplastic materials that have not only osteoinductive and osteoconductive properties but are also convenient for use. In the study, compositions based on collagen hydrogel were developed. Polylactide granules (PLA) or a traditional bone graft, a mixture of hydroxyapatite and β-tricalcium phosphate (HAP/β-TCP), were used for gel filling to improve mechanical osteoconductive properties of compositions. The mechanical tests showed that collagen hydrogels filled with 12 wt% highly porous PLA granules (elastic modulus 373 ± 55 kPa) or 35 wt% HAP/β-TCP granules (elastic modulus 451 ± 32 kPa) had optimal manipulative properties. All composite components were cytocompatible. The cell’s viability was above 90%, and the components’ structure facilitated the cell’s surface adhesion. The bone morphogenetic protein-2 (BMP-2) provided osteoinductive composition properties. It was impregnated directly into the collagen hydrogel with the addition of fibronectin or inside porous PLA granules. The implantation of a collagen hydrogel with BMP-2 and PLA granules into a critical-size calvarial defect in rats led to the formation of the most significant volume of bone tissue: 61 ± 15%. It was almost 2.5 times more than in the groups where a collagen-fibronectin hydrogel with a mixture of HAP/β-TCP (25 ± 7%) or a fibronectin-free composition with porous PLA granules impregnated with BMP-2 (23 ± 8%) were used. Subcutaneous implantation of the compositions also showed their high biocompatibility and osteogenic potential in the absence of a bone environment. Thus, the collagen-fibronectin hydrogel with BMP-2 and PLA granules has optimal biocompatibility, osteogenic, and manipulative properties.

Background. Mineralized lesions of the jaws are often found incidentally on radiographs and computed tomography. Most of them are benign, and only a few rare cases are associated with malignant transformation. However, there is little clinical data on successful rehabilitation with implants in patients with mineralized lesions. This narrative review aimed to study the efficiency and safety of dental implantation in the area of hyperdense lesions. Materials and Methods. A PubMed, Google Scholar, and Science Direct database search was carried out with keywords and manually. Results. The literature exploration identified 323 articles; only 19 of them matched the search criteria and reported cases about dental implantation in the lesion area. It has been shown that in 84.2% of described cases, dental implantation was successful: in the osteoid osteoma, odontoma, cementoblastoma, idiopathic osteosclerosis, and condensing osteitis areas dental implantation was performed without any complications. The possibility of lesion recurrence and implant failure limited the use of dental implants in the area of osteoblastoma and cemento-osseous dysplasia. Although most cases of dental implantation in hyperdense jaw lesions were successful and were not accompanied by complications, further research is needed.

Background/Objectives: The replenishment of bone deficiency remains a challenging task in clinical practice. The use of gene-activated matrices (GAMs) impregnated with genetic constructs may be an innovative approach to solving this problem. The aim of this work is to develop collagen-based matrices with the addition of platelet-rich plasma, carrying polyplexes with the BMP2 gene, to study their biocompatibility and osteogenic potential in vitro and in vivo. Methods: The cytocompatibility of the materials during incubation with adipose-derived stem cells (ADSCs) was studied using the MTT test and fluorescent microscopy. Biocompatibility was assessed during intramuscular implantation, followed by histological analysis. Osteogenic differentiation was determined by the expressions of Alpl and Bglap using real-time PCR and extracellular matrix (ECM) mineralization by alizarin red staining. The efficiency of bone regeneration was studied using micro-CT and analysis of histological sections stained according to Masson. Results: After the incubation of ADSCs with GAS, significant increases in the expressions of the Alpl and Bglap genes by 3 ± 0.1 and 9.9 ± 0.6 times, relative to the control, as well as mineralization of the ECM, were observed. The volume of newly formed bone was 37.2 ± 6.2% after implantation of GAS, 20.9 ± 1.2%—non-activated Col/PRP, and 2.6 ± 1.5% in an empty defect. Conclusions: The use of Col/PRP-based matrices is an effective method for delivering of the osteoinductor gene to the site of bone tissue damage. The highest degree of healing was observed after the implantation of Col/PRP-TF/pBMP2 into the critical size defect compared to the other groups.

The restoration of bone defects resulting from tooth loss, periodontal disease, severe trauma, tumour resection and congenital malformations is a crucial task in dentistry and maxillofacial surgery. Growth factor- and gene-activated bone graft substitutes can be used instead of traditional materials to solve these problems. New materials will overcome the low efficacy and difficulties associated with the use of traditional bone substitutes in complex situations. One of the most well-studied active components for bone graft substitutes is bone morphogenetic protein-2 (BMP-2), which has strong osteoinductive properties. The aim of this review was to examine the use of BMP-2 protein and gene therapy for bone regeneration in the oral and maxillofacial region and to discuss its future use.

The use of 3D-printed gene-activated bone grafts represents a highly promising approach in the fields of dentistry and orthopedics. Bioresorbable poly-lactic-co-glycolic acid (PLGA) scaffolds, infused with adenoviral constructs that carry osteoinductive factor genes, may provide an effective alternative to existing bone grafts for the reconstruction of extensive bone defects. This study aims to develop and investigate the properties of 3D scaffolds composed of PLGA and adenoviral constructs carrying the BMP2 gene (Ad-BMP2), both in vitro and in vivo. The elastic modulus of the disk-shaped PLGA scaffolds created using a specialized 3D printer was determined by compressive testing in both axial and radial directions. In vitro cytocompatibility was assessed using adipose-derived stem cells (ADSCs). The ability of Ad-BMP2 to transduce cells was evaluated. The osteoinductive and biocompatible properties of the scaffolds were also assessed in vivo. The Young’s modulus of the 3D-printed PLGA scaffolds exhibited comparable values in both axial and radial compression directions, measuring 3.4 ± 0.7 MPa for axial and 3.17 ± 1.4 MPa for radial compression. The scaffolds promoted cell adhesion and had no cytotoxic effect on ADSCs. Ad-BMP2 successfully transduced the cells and induced osteogenic differentiation in vitro. In vivo studies demonstrated that the 3D-printed PLGA scaffolds had osteoinductive properties, promoting bone formation within the scaffold filaments as well as at the center of a critical calvarial bone defect.

In dentistry, maxillofacial surgery, traumatology, and orthopedics, there is a need to use osteoplastic materials that have not only osteoinductive and osteoconductive properties but are also convenient for use. In the study, compositions based on collagen hydrogel were developed. Polylactide granules (PLA) or a traditional bone graft, a mixture of hydroxyapatite and β-tricalcium phosphate (HAP/β-TCP), were used for gel filling to improve mechanical osteoconductive properties of compositions. The mechanical tests showed that collagen hydrogels filled with 12 wt% highly porous PLA granules (elastic modulus 373 ± 55 kPa) or 35 wt% HAP/β-TCP granules (elastic modulus 451 ± 32 kPa) had optimal manipulative properties. All composite components were cytocompatible. The cell’s viability was above 90%, and the components’ structure facilitated the cell’s surface adhesion. The bone morphogenetic protein-2 (BMP-2) provided osteoinductive composition properties. It was impregnated directly into the collagen hydrogel with the addition of fibronectin or inside porous PLA granules. The implantation of a collagen hydrogel with BMP-2 and PLA granules into a critical-size calvarial defect in rats led to the formation of the most significant volume of bone tissue: 61 ± 15%. It was almost 2.5 times more than in the groups where a collagen-fibronectin hydrogel with a mixture of HAP/β-TCP (25 ± 7%) or a fibronectin-free composition with porous PLA granules impregnated with BMP-2 (23 ± 8%) were used. Subcutaneous implantation of the compositions also showed their high biocompatibility and osteogenic potential in the absence of a bone environment. Thus, the collagen-fibronectin hydrogel with BMP-2 and PLA granules has optimal biocompatibility, osteogenic, and manipulative properties.