Lignin is a widely abundant renewable source of phenolic compounds. Despite the growing interest on using it as a substitute for its petroleum-based counterparts, only 1 to 2% of the global lignin production is used for obtaining value-added products. Lignosulphonates (LS), derived from the sulphite pulping process, account for 90% of the total market of commercial lignin. The most successful industrial attempts to use lignin for wood adhesives are based on using this polymer as a partial substitute in phenol-formaldehyde or urea-formaldehyde resins. Alternatively, formaldehyde-free adhesives with lignin and lignosulphonates have also been developed with promising results. However, the low number of reactive sites available in lignin’s aromatic ring and high polydispersity have hindered its application in resin synthesis. Currently, finding suitable crosslinkers for LS and decreasing the long pressing time associated with lignin adhesives remains a challenge. Thus, several methods have been proposed to improve the reactivity of lignin molecules. In this paper, techniques to extract, characterize, as well as improve the reactivity of LS are addressed. The most recent advances in the application of LS in wood adhesives, with and without combination with formaldehyde, are also reviewed.

Wood-based products usually have serious limitations concerning contact with water, both because wood is a hygroscopic material and because the commonly used binder has low moisture resistance. This paper studies the effect of panel moisture content (MC) on the physico-mechanical properties of medium density fiberboards (MDF). Several commercial MDF boards produced in Europe were stored at room temperature and relative humidity (RH) for 9 weeks (approx. range 15–20 °C and 50–85% RH). Every week, a strip of each MDF board was cut out, divided into 5 × 5 cm test pieces and its internal bond strength (IB) was measured. A strong influence of MDF moisture content on internal bond strength was observed and therefore IB test pieces were stored in a climatic chamber (either at 20 °C, 55% RH and at 20 °C, 70% RH). A decreasing linear relation was established between IB and MC. It was found that this effect is reversible: after drying, internal bond strength rises again (following a slight hysteresis). This work reinforces the importance of conditioned storage before board properties analysis, as described in European Standard EN 319.

Currently, the majority of binders used in wood particleboard (PB) manufacturing are formaldehyde-based synthetic resins. Because of the toxicity of formaldehyde, there is a strong demand for eco-friendly alternatives with similar performances and economic viability. In this work, thick spent sulfite liquor (TSSL), an industrial byproduct from sulfite pulp mills, is proposed as a binder for fully bio-based PBs. The results showed that PBs bound with TSSL present appropriate mechanical performance, which was further improved when TSSL was combined with wheat flour at an 84:16 dry weight ratio and preheated to 94 °C prior to application. For 13.2% binder content per dry wood weight, the PB internal bond strength was 0.46 N mm⁻², which is above the standard requirements for PB type P2 (0.35 N mm⁻²). Optical microscopy showed that TSSL hinders the gelatinization of starch granules during preheating, allowing the binder mixture to maintain a low viscosity suitable for combination with wood particles and PB production.

Melamine-formaldehyde is the most common resin used in the production of high-pressure laminates and low-pressure laminates (melamine impregnated paper), due to its properties of durability, good fire, and heat resistance and good moisture resistance. High-pressure laminate is a common choice for horizontal and vertical applications in the construction and furniture industries, thanks to its durability and versatility. The manufacture of such laminates commonly starts with the impregnation of decorative and kraft papers with thermosetting resins and after a drying process, the impregnated paper sheets are bonded together by high pressure and temperature pressing. The aim of this work was to evaluate the influence of the melamine-formaldehyde resins condensation degree after synthesis on high-pressure laminates performance. For that purpose, melamine-formaldehyde resins with different condensation degree were synthetized and characterized. Fourier-transform infrared–attenuated total reflection spectroscopy and dynamic mechanical analysis were used to study the chemical and mechanical cure of melamine-formaldehyde resins. Melamine-formaldehyde condensation degree has shown to have influence on resin pot-life, on characteristic reaction temperatures, on the degree of cross-linking achieved, and finally on the surface quality of high-pressure laminates.

This work studies the use of soy protein as a natural formaldehyde scavenger in wood particleboard production. The protein is incorporated in two forms: a) as a powder, during the blending process of wood particles with urea-formaldehyde binder resin, and b) as an aqueous solution, added at different times during resin synthesis. Analysis of variance (ANOVA) was used to evaluate the significance level of two effects (amount of added soy and time of addition) on internal bond strength, thickness swelling, and formaldehyde content of the resulting panels. The results showed that soy protein can contribute to decrease the formaldehyde content of particleboard panels. Addition in powder form or in solution during the resin condensation step leads to the highest formaldehyde reduction, without significantly affecting the physical properties of the panels.